| Titre : |
Preparation of crosslinkable cationic polyacrylate latex and its film properties |
| Type de document : |
texte imprimé |
| Auteurs : |
Xueke Zhang, Auteur ; Kaimin Chen, Auteur ; Ziwei Li, Auteur ; Qianqian Zhang, Auteur ; Chenming Xu, Auteur ; Yue Chang, Auteur ; Shaoguo Wen, Auteur |
| Année de publication : |
2024 |
| Article en page(s) : |
p. 341-354 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Bases (chimie)
Humidité -- Absorption:Eau -- Absorption
Latex
Polyacrylates
Polymères cationiques
Polymérisation en émulsion
Résistance chimique
Revêtements -- Propriétés mécaniques
Revêtements organiques
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Cationic polyacrylate latex has attracted extensive attention due to its special properties and potential applications in wood primers, metal coatings, and fabric treatments, etc. However, cationic polyacrylate latex has poor durability and stability, which limits its use in practical applications. In this study, a functional cationic monomer (3-chloro-2-hydroxypropyl) dimethyl [2-[(2-methyl-1-oxoallyl)oxy]ethyl] ammonium chloride (DEAC) was combined with two conventional monomers of methyl methacrylate (MMA) and butyl acrylate (BA) to prepare cationic polyacrylate latex by a semi-continuous emulsion polymerization. The obtained latexes showed typical cationic character with zeta potential in the range of + 40 to + 65 mV. The effect of DEAC on the stability of latex was studied and good alkali resistance could be gained at high DEAC content. Water resistance and mechanical properties of the film before and after crosslinking are studied in detail. The results showed that the water absorption reduced from 60.04% to a minimum of 9.18%, and the tensile strength increased from 3.9 to 8.4 MPa, which was comparable to solvent-based polyacrylate films. This work provides a new strategy for the preparation of waterborne cationic polyacrylate latex with improved water resistance and good mechanical properties, etc., which can be applied in papermaking, textiles, wood primers, and other potential fields. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Synthesis of DEAC - Synthesis of cationic polyacrylate latex P(MMA-co-BA-co-DEAC) - Preparation of cationic polyacrylate film - Characterization
- RESULTS AND DISCUSSION : Effect of DEAC on polyacrylate latex - Effect of DEAC on stability properties - Film properties
- Table 1 : Properties of cationic polyacrylate latex with different amounts of DEAC
- Table 2 : Properties of cationic polyacrylate latex with different amount of DEAC |
| DOI : |
https://doi.org/10.1007/s11998-023-00826-y |
| En ligne : |
https://drive.google.com/file/d/143nNUjIN202dKWmu9uZH5XyWG-Zz61cy/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40457 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 1 (01/2024) . - p. 341-354
Aller sur edunet
Accueil
Preparation of crosslinkable cationic polyacrylate latex and its film properties in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 1 (01/2024)