Synthesis of poly(propylene carbonate) diol-based waterborne polyurethane modified by epoxy resin with anticorrosion properties |
| Type de document : |
texte imprimé |
| Auteurs : |
Yiheng Xiao, Auteur ; Wei Ou, Auteur ; Zonglin He, Auteur ; Zhu Ding, Auteur ; Jiaoyan Ai, Auteur ; Lina Song, Auteur ; Baohua Liu, Auteur |
| Année de publication : |
2024 |
| Article en page(s) : |
p. 319-328 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Adhésion
Anticorrosifs
Anticorrosion
Caractérisation
Epoxydes
Essai Wolff-Wilborn
Polymères -- Synthèse
Polymères en émulsion
Polyuréthanes
Revêtements en phase aqueuse
Revêtements organiques
Revêtements protecteurs
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
A series of modified waterborne polyurethane (WPU) with various epoxy contents was synthesized from poly (propylene carbonate) diol (PPCD)-based polyurethane prepolymer and ring-opening epoxy resin (RO-EP). The particle size, storage stability, and freeze-thaw resistance of the emulsions were examined. The pencil hardness and adhesion level of the films were tested. The structure of the modified waterborne polyurethane was characterized by Fourier transform infrared spectroscopy. The thermal stability of the modified waterborne polyurethane was studied by thermogravimetric analysis. The corrosion resistance of emulsion coating was tested by the salt spray test and electrochemical impedance spectroscopy (EIS). The waterborne polyurethane emulsion modified by RO-EP had excellent storage stability. When the content of the ring-opening epoxy resin was 10 wt%, the particle size of WPU was the smallest. The corresponding coating had excellent hardness and adhesion level. The salt spray and EIS test showed that the WPU coating with 10% RO-EP had superior corrosion resistance. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Preparation of RO-EP - Preparation of E-WPU - Preparation of E-WPU films - Characterization
- RESULTS AND DISCUSSION : Fourier transform infrared spectroscopy (FTIR) analysis - TGA analysis - Particle size analysis - Adhesion and hardness test analysis - Salt spray test - EIS measurement
- Table 1 : Reactant proportions of WPU and E-WPU
- Table 2 : TGA data of WPU and E-WPU films with various RO-EP contents
- Table 3 : Properties of WPU and E-WPU emulsions
- Table 4 : Adhesion level and pencil hardness of WPU and E-WPU films
- Table 5 : Impedance modulus of coatings at different time |
| DOI : |
https://doi.org/10.1007/s11998-023-00823-1 |
| En ligne : |
https://drive.google.com/file/d/14Xy6b0xZPvCh7CAHet2LxIJwwjmj0GlQ/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40450 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 1 (01/2024) . - p. 319-328
Aller sur edunet
Accueil
Synthesis of poly(propylene carbonate) diol-based waterborne polyurethane modified by epoxy resin with anticorrosion properties in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 1 (01/2024)