Corrosion behavior of AISI 316 stainless steel coated with modified fluoropolymer in marine condition / E. Husain in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 5 (09/2018)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 5 (09/2018) . - p. 945-955 Titre : Corrosion behavior of AISI 316 stainless steel coated with modified fluoropolymer in marine condition Type de document : texte imprimé Auteurs : E. Husain, Auteur ; A. Abdel Nazeer, Auteur ; J. Alsarraf ; K. Al-Awadi ; M. Murad ; A. Al-Naqi ; A. Shekeban Année de publication : 2018 Article en page(s) : p. 945-955 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier inoxydable Anticorrosifs Anticorrosion Atmosphère marine Caractérisation Essais d'adhésion Métaux -- Revêtements protecteurs Morphologie (matériaux) Mouillabilité Nanoindentation Polyfluorure de vinylidène Polyméthacrylate de méthyle Le poly(méthacrylate de méthyle) (souvent abrégé en PMMA, de l'anglais Poly(methyl methacrylate)) est un polymère thermoplastique transparent obtenu par polyaddition dont le monomère est le méthacrylate de méthyle (MMA). Ce polymère est plus connu sous son premier nom commercial de Plexiglas (nom déposé), même si le leader global du PMMA est Altuglas International9 du groupe Arkema, sous le nom commercial Altuglas. Il est également vendu sous les noms commerciaux Lucite, Crystalite, Perspex ou Nudec. Spectroscopie d'impédance électrochimique Spectroscopie Raman Index. décimale : 667.9 Revêtements et enduits Résumé : In the maritime industry, stainless steel corrosion resistance requires further surface improvement and further enhanced protection using surface coatings. In this study, an engineered copolymer of polyvinylidene fluoride (PVDF) with polymethylmethacrylate (PMMA)-blended coating was found to provide outstanding corrosion resistance for metal surfaces affording protection against severely corrosive marine environments. Electrochemical measurements indicate that corrosion protection of 316 stainless steel was drastically increased when utilizing the KP blend (a combination of PVDF + PMMA), producing a new set of corrosion properties and morphological characteristics. The corrosion protection of the KP coating proved to be very effective in reducing the passive region current density from 2.19 × 10−5 A/cm2 (for bare stainless steel) to 2.63 × 10−10 A/cm2 and the breakdown passive region potential at 0.25 V. This was followed by a significant decrease in corrosion rate, when compared to pure PMMA and PVDF films, during exposure to artificial marine seawater. With the KP film, impedance measurements surpassed those of other films, with a noticeable nonpeak straight line in the phase angle diagram. Optical observation showed that corrosion pits and delamination areas existed under the coatings. Note de contenu : - EXPERIMENTAL PROCEDURE : Material - Synthesization of coating fils - Surface characterization - Electrochemical measurements - Raman spectra - Nanoindentation measurements - RESULTS AND DISCUSSION : Wettability of the stainless steel alloy-coated surfaces - Adhesion test - Raman spectroscopy - Potentiodynamic polarization - Electrochemical impedance spectroscopy - Surface morphology - Nanoindentation analysis DOI : 10.1007/s11998-017-0025-4 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-0025-4.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=31119 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20232	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)