Preparation in presence of urushiol and properties of acrylate latex with interparticle bridges / Jianhong Yang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 4 (07/2018)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 4 (07/2018) . - p. 819-830 Titre : Preparation in presence of urushiol and properties of acrylate latex with interparticle bridges Type de document : texte imprimé Auteurs : Jianhong Yang, Auteur ; Qin Shen, Auteur ; Fengqin Shen, Auteur ; Jun Cai, Auteur ; Wanghui Liu, Auteur ; Ming Zhou, Auteur Année de publication : 2018 Article en page(s) : p. 819-830 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Angle de contact Caractérisation Humidité -- Absorption:Eau -- Absorption Latex Polyacrylates Polymérisation en émulsion Potentiel zeta Résonance magnétique nucléaire Revêtements -- Propriétés mécaniques Revêtements -- Propriétés thermiques Spectrométrie infrarouge Urushiol L’urushiol est une toxine organique que l'on trouve dans les plantes de la famille des Anacardiaceae, spécialement dans le genre Toxicodendron (par exemple le sumac grimpant en Amérique du Nord). Il provoque des allergies de la peau ou dermatites, pouvant être importantes, au contact de ces plantes. Le nom vient du mot japonais urushi (漆?), qui désigne une laque produite dans l'Asie orientale à partir du suc des arbres kiurushi (arbre à laque). L'oxydation et la polymérisation de l'urushiol dans le suc de l'arbre en présence d'humidité permet de former une laque dure utilisée traditionnellement pour produire des objets d'art laqués en Chine et au Japon. Index. décimale : 667.9 Revêtements et enduits Résumé : Acrylate latices were prepared by seeded emulsion polymerization of methyl methacrylate (MMA) and butyl acrylate (BA) in presence of urushiol with multifunctional groups (0–6 wt%). The emulsion polymerization was strongly influenced by the urushiol content. With increasing urushiol content, the conversion rate of the monomers first increased then decreased, the stability of emulsion polymerization gradually declined, the average particle size of the latex increased from 115.9 to 175.3 nm, and a change from mono- to bimodal particle size distribution occurred. Interestingly, transmission electron microscopy (TEM) showed that some particles were connected by linear bridges in presence of urushiol. Based on results of 1H nuclear magnetic resonance (NMR) analysis, such formation of interparticle bridges is due to participation of urushiol in the emulsion polymerization of the acrylate monomers. The content of urushiol also affected the properties of latex films. With increasing urushiol content from 0 to 3 wt%, the adhesion, pencil hardness, and contact angle were markedly improved from grade 6 to grade 2, from B to 3H, and from 22° to 61°, respectively, due to formation of interparticle bridges. When the content of urushiol exceeded 3 wt%, the adhesion and pencil hardness remained unchanged, but the water contact angle markedly declined because of higher surface roughness of the latex film. Furthermore, addition of urushiol enhanced the thermal stability of the latex films. Note de contenu : - EXPERIMENTAL : Materials - Preparation of acrylate latex - Preparation of acrylate latex films - Characterization - RESULTS AND DISCUSSION : IR spectra - H NMR analysis - Average size and zeta potential of latex particles - Conversion and coagulation rate - Contact angle and water absorption - Thermal properties - Mechanical properties DOI : 10.1007/s11998-017-0023-6 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-0023-6.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30859 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20078	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)