| Titre : |
Correlation analysis concerning the physical and mechanical properties of composites made of chromium leather scraps-chloroprene rubber adhesive RL-CR |
| Type de document : |
texte imprimé |
| Auteurs : |
Dongsheng Xin, Auteur ; Yurui Xin, Auteur ; Yinghua Ma, Auteur |
| Année de publication : |
2023 |
| Article en page(s) : |
p. 83-87 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Allongement à la rupture
Assemblages collés
Caoutchouc
Composites -- Propriétés mécaniques
Composites -- Propriétés physiques
Cuirs et peaux -- Déchets -- Recyclage
Eclatement (matériaux)
Humidité -- Absorption:Eau -- Absorption
Mouillabilité
Perméabilité
Polychloroprène
Traction (mécanique)
|
| Index. décimale : |
675 Technologie du cuir et de la fourrure |
| Résumé : |
In this paper, the pearson product moment correlation coefficient analysis method is used to show that the tensile strength of RL/CR is highly positively correlated with the elongation at break, the bursting height is highly positively correlated with the bursting strength, the tensile strength is highly positively correlated with the bursting strength, and the bursting height is negatively correlated with the elongation at break. The air permeability of RL/CR is not correlated with 15 minutes water absorption, but is negatively correlated with 24 hours water absorption and surface wettability ; The 15 minutes water absorption of RL/CR is negatively correlated with the 24 hours water absorption and the surface wettability ; The surface wettability is positively correlated with 24 hours water absorption.
The tensile strength of RL/CR is negatively correlated with air permeability, highly positively correlated with 15 minutes and 24 hours water absorption, and highly negatively correlated with surface wettability. The bursting strength of RL/CR is negatively correlated with air permeability and 15 min water absorption, and highly positively correlated with 24 hours water absorption and surface wettability. |
| Note de contenu : |
- Introduction to correlation analysis of RL/CR
- Theoretical basis of correlation analysis method
- Experimental design of the orthogonal preparation of RL/CR and determination of its physical and mechanical properties
- Calculation of correlation coefficient of physical and mechanical properties of RL/CR
- Correlation analysis of physical and mechanical properties of RL/CR
- Table 1 : Factors and levels of orthogonal test
- Table 2 : Hot pressing process with orthogonal test
- Table 3 : Mechanical properties of orthogonal test
- Table 4 : Physical performance of orthogonal test
- Table 5 : Correlation analysis of physical and mechanical properties of L5
- Table 6 : Correlation analysis of physical and mechanical properties of L9
- Table 7 : Correlation analysis of physical and mechanical properties of L3
- Table 8 : Correlation analysis of physical and mechanical properties of L5, L9, L3
- Table 9 : Relevance of physical and mechanical properties of RL/CR |
| En ligne : |
https://drive.google.com/file/d/1Vw7-aw4Zt9ocWQM7WPhmaKQWLEg0gqAG/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39577 |
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 107, N° 3 (05-06/2023) . - p. 83-87
Aller sur edunet
Accueil
Correlation analysis concerning the physical and mechanical properties of composites made of chromium leather scraps-chloroprene rubber adhesive RL-CR in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC), Vol. 107, N° 3 (05-06/2023)