Application issue of anthraquinonoid vat dyes on inherently flame-resistant fabrics |
| Type de document : |
texte imprimé |
| Auteurs : |
Martinia Glogar, Auteur ; Tanja Pusic, Auteur ; Veronika Lovreskov, Auteur ; Tea Kaurin, Auteur ; Ana Sutlovic, Auteur |
| Année de publication : |
2023 |
| Article en page(s) : |
p. 190-199 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Anthraquinone
Fibre aramide
IgnifugeantsComposé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface.
Indice limite d'oxygèneL'indice limite d'oxygène (ILO), ou indice d'oxygène (limite) (IO(L)) ou (L)OI (limiting) oxygen index en anglais), est une grandeur et un essai de laboratoire à petite échelle permettant de caractériser la combustibilité (inflammabilité) d'un matériau combustible, notamment une matière plastique (ou un polymère). Ce critère donne une indication relative de la combustibilité dans des conditions d'essai spécifiées, définies par des normes. Il existe différentes normes selon les domaines d'application1 et les pays : ISO 4589, ASTM D2863, UL 94, etc. Il ne faut pas confondre cette propriété avec la concentration limite en oxygène qui donne la concentration minimale en oxygène dans un mélange avec un combustible permettant l'inflammation en présence d'une source d'ignition.
Solidité de la couleur
Teinture -- Fibres textiles synthétiques
Textiles et tissus -- Analyse
Textiles et tissus -- Propriétés tactiles
|
| Index. décimale : |
667.3 Teinture et impression des tissus |
| Résumé : |
The vat dyeing process of specific fabrics with protective, inherently fire retardant properties that have a high content of aramid fibres in their composition, is presented. The research was performed on fabric samples that differ in raw material composition and aramid content. The samples were dyed in raw form (group 1) as well as after pretreatment with alkaline scouring (group 2). Measured limiting oxygen index (LOI) values showed that the selected fabrics meet the properties of inherently fire retardant fabrics. Dyeing was performed with Indanthren® Olive Green HB (manufactured by DyStar) vat dye, in exhaustion process, with a bath ratio of 1:30. The dye concentration was 3%, and sodium-hydrosulphite (Na2S2O4) was used as a reducing agent. The colouristic analyses were performed based on spectrophotometric measurement and results interpretation according to CIELab system. The evaluation of primary tactile properties was performed which show an increase of smoothness and softness after scouring and dyeing. Also, wash fastness as well as light fastness tests have shown satisfactory fastness properties. |
| Note de contenu : |
- Limiting oxygen index (LOI)
- Dyeing
- Colour fastness and tactile properties testing
- Spectrophotometric measurement
- Microscopic imaging
- Table 1 : Composition of analysed fabrics
- Table 2 : Constructional and mechanical characteristics of fabrics
- Table 3 : Recipe and conditions of alkaline scouring
- Table 4 : Limiting oxygen index (LOI) of fabrics
- Table 5 : Primary tactile properties of dyed fabrics
- Table 6 : Colour strength (K/S) values of dyed samples |
| DOI : |
https://doi.org/10.1111/cote.12661 |
| En ligne : |
https://onlinelibrary.wiley.com/doi/epdf/10.1111/cote.12661 |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39531 |
in COLORATION TECHNOLOGY > Vol. 139, N° 2 (04/2023) . - p. 190-199
Aller sur edunet
Accueil
Application issue of anthraquinonoid vat dyes on inherently flame-resistant fabrics in COLORATION TECHNOLOGY, Vol. 139, N° 2 (04/2023)