| Titre : |
Moving beyond the 25-year coating |
| Type de document : |
texte imprimé |
| Auteurs : |
Todd Williams, Auteur ; Ahren Olson, Auteur ; Paul Vinik, Auteur |
| Année de publication : |
2018 |
| Article en page(s) : |
p. 42-53 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Adhésion
Composés inorganiques
Composés organiques
Corrosion
Essais accélérés (technologie)
Essais de résilience
Primaire (revêtement)
Revêtements -- Finition:Peinture -- Finition
Revêtements multicouches
Zinc
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Zinc-rich primers have been well studied, yet specifying inorganic (IOZ) or organic zinc (OZ) for three-coat systems remains a highly debated topic. During the 1960s and 1970s inorganic zincs became the dominant primer in North America and published literature shows IOZ outperforming OZ in three-coat systems. The study presented in this article focuses on evaluating two variables within the traditional ZEU system that could impact performance — zinc-rich primer type (i.e., inorganic or organic) and topcoat chemistry. |
| Note de contenu : |
- Adhesion
- Accelerated corrosion testing
- Natural corrosion testing
- Accelerating weathering
- Natural weathering
- TABLES : 1. Description of coatings applied and evaluated in study - 2. Average dry-film thickness of each coat of three-coat systems - 3. NEPCOAT Coating Performance Requirements
- FIGURES : 1. Panels attached to a rack at the natural weathering site in the Florida Keys. The rack is facing south and panels are exposed at a 45 degree angle from vertical - 2. Tensile adhesion results ; asterisk denotes glue-to-topcoat failure - 3. Scribe creep data after 5,000 hours of B117 exposure - 4. Data from 5,040 hours of D5894 testing - 5. Blistering of Coatings After 4,032 Hours Cyclic Prohesion (ASTM D5894) - 6. Panels after 54 months of exposure at Tea Table Key - 7. QUV-A data after 5,000 hours of exposure per ASTM 4587 cycle 2 - 8. Color retention data after 5,000 hours of exposure per ASTM D4587 cycle 2 - 9. Gloss retention in natural weathering after 54 months of exposure at Tea Table Key - 10. Color retention in natural weathering after 54 months of exposure at Tea Table Key |
| En ligne : |
http://www.paintsquare.com/archive/?fuseaction=view&articleid=6209 |
| Format de la ressource électronique : |
Web |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30362 |
in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL) > Vol. 34, N° 12 (12/2017) . - p. 42-53
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheMoving beyond the 25-year coating / Todd Williams in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL), Vol. 34, N° 12 (12/2017)