Structure–property correlations of foul release coatings based on low hard segment content poly(dimethylsiloxane–urethane–urea) / Sangram K. Rath in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 1 (01/2018)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 1 (01/2018) . - p. 185-198 Titre : Structure–property correlations of foul release coatings based on low hard segment content poly(dimethylsiloxane–urethane–urea) Type de document : texte imprimé Auteurs : Sangram K. Rath, Auteur ; Jayesh G. Chavan, Auteur ; Tanaji K. Ghorpade, Auteur ; T. Umasankar Patro, Auteur ; Manoranjan Patri, Auteur Année de publication : 2018 Article en page(s) : p. 185-198 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Copolymère uréthane-urée Polydiméthylsiloxane Le polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones. Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone. Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK). La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Revêtements antisalissures:Peinture antisalissures Salissures biologiques Index. décimale : 667.9 Revêtements et enduits Résumé : We report the foul release characteristics of model poly(dimethylsiloxane–urethane–urea) (PDMSPU)-based coatings with a relatively lower hard segment content of 9 to 13.7 wt%. The PDMSPUs were prepared by facile moisture curing of isophorone diisocyanate-capped hydroxyalkyl-terminated PDMS. The surface free energies of the coatings were tuned (20–25 mJ/m2) by varying the hard segment content to be in the minimum adhesive regime (20–30 mJ/m2) of Baier’s curve pertaining to the relative amount of biofouling vs the critical surface tension of various chemical substrates. A series of complimentary analytical tools, namely 1H NMR spectroscopy, small-angle x-ray scattering (SAXS), FTIR-attenuated total reflectance spectroscopy (FTIR-ATR), contact angle goniometry, marine field tests, and quantitative biofouling adhesion in shear, have been employed to deduce several physicochemical parameters of importance to establish the structure property correlations. Further, the time-dependant changes in surface wettability and surface concentration of polar functional groups of the coatings (immersed in 3.5 wt% aqueous solution of NaCl) were investigated by FTIR-ATR and contact angle goniometry. The extent of surface restructuring was found to increase with increasing hard segment content of the PDMSPUs and consequently increasing attachment strengths of macrofoulants with the coatings, which were in the range 0.12–0.5 MPa. Note de contenu : - Identification of the structure of PDMSPU - Phase morphology and surface properties - Macrofouling behavior and foul release characteristics - Surface restructuring kinetics and mechanism DOI : 10.1007/s11998-017-9982-x En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-9982-x.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30111 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
19610	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)