Microwave-assisted polyol synthesis of V–ZrSiO4 nanoparticles and its use as a blue ceramic pigment |
| Type de document : |
texte imprimé |
| Auteurs : |
Hossein Heydari, Auteur ; Mardali Yousefpour, Auteur ; Esmaeil Emadoddin, Auteur ; Maryam Hosseini Zori, Auteur ; Mohsen Khajeh Aminian, Auteur |
| Année de publication : |
2022 |
| Article en page(s) : |
p. 1595-1607 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Bleu (couleur)
Caractérisation
Colorimétrie
Dispersions et suspensions
Matériaux céramiques
Micro-ondes
Pigments inorganiques
Polymères -- Synthèse
Polyols
ZirconLe zircon est un minéral du groupe des silicates, sous-groupe des nésosilicates. De composition ZrSiO4, c'est un silicate de zirconium naturel. Ses cristaux font partie des pierres fines de la joaillerie.
Le mot zircon proviendrait, soit de l'arabe zarqun (cinabre), soit du persan zargun (doré). On retrouve cette étymologie dans l'anglais jargoon, qui désigne des zircons de couleur claire. Les zircons jaunes à grenat sont appelés hyacinthes (du grec signifiant "jacinthe"). Les spécimens transparents sont utilisés en joaillerie pour des utilisations similaires à celles du diamant.
Le terme de zircon est parfois utilisé à tort pour désigner la zircone, l'oxyde de zirconium de composition ZrO2. La zircone à l'état naturel (minéral baddeleyite (en)) est extraite industriellement pour servir de substitut peu onéreux au diamant. (Wikipedia)
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
In this study, a microwave-assisted polyol technique was used to synthesize vanadium-containing nanopigments of ZrSiO4. The influence of microwave power (300–900 W) and irradiation time (60–120 s) on the purity, crystallinity, and particle size of the synthesized nanoparticles was studied. The resulting powder (synthesized and calcined) was investigated by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM). XRD analysis shows that the 300 W synthesized powder is composed of solid amorphous particles. The microwave power was increased to 900 W to convert all particles to crystalline nano-ZrSiO4. The experiment revealed the critical influence of irradiation time and microwave power on purity and crystallinity. The microwave effect can accelerate the reaction and the nucleation rate of ZrSiO4 at a lower reaction temperature. The nanoparticles obtained were tested as ceramic pigments, and the colorimetric parameters of CIELab were measured. Structure and colorimetric studies have confirmed that a fully crystalline zircon phase can be obtained at 1100°C and can be used as a blue pigment. |
| Note de contenu : |
- EXPERIMENTAL PROCEDURE : Precursor and reagents - Preparation of suspensions - Techniques of characterization
- RESULTS AND DISCUSSION : Synthesis and characterization of suspensions - Effect of microwave power and irradiation time on crystallinity - Microstructure investigation - Colorimetric results
- Table 1 : Sample preparation conditions for different microwave power and irradiation time in EG solvent
- Table 2 : CIELab values of the glazes provided by pigments calcined at 1100°C |
| DOI : |
https://doi.org/10.1007/s11998-022-00632-y |
| En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-022-00632-y.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38292 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 5 (09/2022) . - p. 1595-1607
Aller sur edunet
Accueil
Microwave-assisted polyol synthesis of V–ZrSiO4 nanoparticles and its use as a blue ceramic pigment in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 5 (09/2022)