[article]
| Titre : |
Mechanical, morphological, thermal and dynamic study of composites of unsaturated polyesters-Date palm leaf Fiber DPLF |
| Type de document : |
texte imprimé |
| Auteurs : |
Abir Berkouk, Auteur ; Ahmed Meghezzi, Auteur ; Hamza Chelali, Auteur ; Mohamed Toufik Soltani, Auteur |
| Année de publication : |
2021 |
| Article en page(s) : |
p. 317-323 |
| Note générale : |
Bibliogr. |
| Langues : |
Français (fre) |
| Catégories : |
Analyse mécanique dynamique
Analyse morphologique
Analyse thermique
Caractérisation
Composites à fibres végétales
Fibres de palmier dattier
Humidité -- Absorption:Eau -- Absorption
Polyesters insaturésLes résines de polyesters insaturés (UP) sont obtenues par polycondensation
d’un ou de plusieurs diacides avec un ou plusieurs glycols, l’un, au moins, des constituants contenant une double liaison éthylénique susceptible de réagir ultérieurement sur un composé vinylique, acrylique ou allylique.
Par le terme résine polyester, on désigne en fait la dissolution du prépolymère polyester insaturé dans un solvant copolymérisable, le plus utilisé étant le styrène. C’est sous cette forme liquide que les résines polyesters sont livrées aux transformateurs.
Après addition de différents adjuvants, charges et renforts, divers procédés de transformation provoquent, sous l’action d’un système catalytique approprié, la copolymérisation finale de la résine en un objet thermodurcissable.
Les polyesters insaturés sont d’un usage relativement ancien (1950), essentiellement
dans le bâtiment (moulage au contact). Ils ont connu un renouveau important à partir de 1980, en particulier au niveau des formulations et de la fiabilité des procédés grâce au développement de technologies industrielles de moulage par injection et par compression dans l’industrie automobile.
|
| Index. décimale : |
668.4 Plastiques, vinyles |
| Résumé : |
In order to improve the properties of unsaturated polyesters, this study discusses the possibilities of developing a natural waste, date palm leaf fiber DPLF, produced in the northern Algerian Sahara, associated with the polymer matrix of a thermosetting polyester resin UP. For this purpose, composite plates containing virgin fiber at rates of 6 and 10% were treated with an alkaline solution of 6% NaOH on the one hand, and a silane compound on the other. In this research, a mechanical study of strength and elongation at break was carried out. In addition, morphological behavior was followed by SEM scanning electron microscopy. ATG thermogravimetric analysis and energy flow were monitored by DSC differential scanning calorimetry. Also, a study of the water absorption capacity has been conducted. In addition, a dynamic mechanical analysis DMA was carried out. The findings of this study show that there is a favorable mechanical behavior for the composites containing the 6% and 10% DPLF fiber, with alkaline NaOH and Silane treatment. They also show that the chemical treatment with alkaline solution and silane gives composites certain thermal stability compared to those with untreated fiber. Findings also explore that the absorption of water by the various composites shows that the chemical treatment promotes some intermolecular associations with water. Findings also show that the storage modulus (E') increases when the composite contains 10% DPLF, treated and untreated, and the maximum value of the tangent moves towards the high temperature for the treated and untreated fiber composite. |
| Note de contenu : |
- MATERIALS AND METHODS : Materials - Chemical treatments of date palm leaf fibers - Fabrication of UP composites - Characterization
- RESULTS AND DISCUSSION : Mechanical analysis of UP/DPLF composites - Morphological study of UP/DPLF composites - Thermogravimetric study of UP/DPLF composites - Differential scanning calorimeter study of UP/DPLF composites - Water absorption of UP/DPLF composites - Dynamic study of UP/DPLF composites
- Table 1. Chemical constituents of leaf date palm fibers
- Table 2. Residual masses at a temperature of 450℃ of the various composites
- Table 3. The decomposition temperature of the different composites |
| DOI : |
https://doi.org/10.18280/rcma.310602 |
| En ligne : |
https://www.iieta.org/download/file/fid/66502 |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37689 |
in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 31, N° 6 (12/2021) . - p. 317-323
[article]
|
Aller sur edunet
Accueil
Mechanical, morphological, thermal and dynamic study of composites of unsaturated polyesters-Date palm leaf Fiber DPLF in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 31, N° 6 (12/2021)