Effective incorporation of ZnO nanoparticles by miniemulsion polymerization in waterborne binders for steel corrosion protection / Stefano Chimenti in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 14, N° 4 (07/2017)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 14, N° 4 (07/2017) . - p. 829-839 Titre : Effective incorporation of ZnO nanoparticles by miniemulsion polymerization in waterborne binders for steel corrosion protection Type de document : texte imprimé Auteurs : Stefano Chimenti, Auteur ; Jesús Manuel Vega, Auteur ; Miren Aguirre, Auteur ; Eva García-Lecina, Auteur ; José Antonio Díez, Auteur ; Hans-Jurgen Grande, Auteur ; María Paulis, Auteur ; Jose Ramon Leiza, Auteur Année de publication : 2017 Article en page(s) : p. 829-839 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Anticorrosion Liants Métaux -- Revêtements protecteurs Miniémulsions Nanoparticules Oxyde de zinc Polymérisation en émulsion Spectroscopie d'impédance électrochimique Index. décimale : 667.9 Revêtements et enduits Résumé : A nanohybrid waterborne binder was synthesized by miniemulsion polymerization with the incorporation of ZnO nanoparticles in order to increase the corrosion protection capability. This system was compared to a neat waterborne binder and to a physical blend of the binder with an aqueous ZnO nanoparticles dispersion. The hybrid dispersion was characterized by SEM and TEM, while the corrosion behavior of these latexes was investigated by electrochemical measurements (open circuit potential and electrochemical impedance spectroscopy in 3.5 wt% NaCl solution), evaluating the effect of the incorporation of these nanoparticles into the polymeric matrix. The incorporation of ZnO nanoparticles by blending showed similar behavior to the neat coating despite flash rust reduction on the metal surface. In contrast, the hybrid binder prepared by miniemulsion polymerization has shown the best performance according to the values of pore resistance (Ri) and coating capacitance (Cc). In general, this study shows how useful can be the miniemulsion polymerization methodology to design hybrid coating formulations, obtaining homogenous distribution of ZnO nanoparticles within the film. Indeed, a heterogeneous distribution can hinder the effectiveness and the corrosion protection capabilities of promising nanoparticles. Note de contenu : - EXPERIMENTAL : Materials - Miniemulsion polymerizations and blend preparation - Coating application - Characterization methods - RESULTS AND DISCUSSION : ZnO nanoparticles wettability - Polymerization kinetics - Film formation - Corrosion evaluation DOI : 10.1007/s11998-017-9958-x En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-9958-x.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=28925 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
19194	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)