Shear-induced 1-D alignment of alumina nanoparticles in coatings |
| Type de document : |
texte imprimé |
| Auteurs : |
Lucas J. Brickweg, Auteur ; Bryce R. Floryancic, Auteur ; Erik D. Sapper, Auteur ; Raymond H. Fernando, Auteur |
| Année de publication : |
2007 |
| Article en page(s) : |
p. 107-110 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Alumine
Matériaux hybrides
Nanoparticules
Nanotechnologie
Polyuréthanes
SiliceLa silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux.
La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...).
Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale.
Vernis
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Atomic Force Microscopy and Scanning Electron Microscopy were used to study shear-induced alignment of alumina and silica nanoparticles in two-component polyurethane clear coatings. 1-D strings of nanoparticles, formed in an extended pearl-necklace fashion were observed near the surfaces of cured films at nanoparticle volume fractions less than 0.05. This alignment is affected by the shear conditions of the application method. When applied by spraying, linear particle strings as long as 5 cm were observed in the direction of shear. Nanoparticle strings were also found, to a lesser extent, when coatings were applied by a drawdown method. The phenomenon was not observed in coatings applied with minimal shear. These particle string formations, in addition to affecting the performance of coatings, may have broader implications in the field of nanomaterials. Our literature searches so far have not uncovered reports of stable, 1-D nanoparticle arrangements with same degree of linearity produced under simple shear with compositions having very low particle loadings. |
| DOI : |
10.1007/s11998-007-9002-7 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-007-9002-7.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=3676 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 4, N° 1 (03/2007) . - p. 107-110
[article]
|
Aller sur edunet
Accueil
Shear-induced 1-D alignment of alumina nanoparticles in coatings in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 4, N° 1 (03/2007)