Morphology and photoluminescence properties of phenolic epoxy resin coating on KH550-modified SrAl2O4: Eu2+, Dy3+ powder in the presence of triarylsulfonium hexafluoroantimonate / Jing Li in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 13, N° 6 (11/2016)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 13, N° 6 (11/2016) . - p. 1075-1082 Titre : Morphology and photoluminescence properties of phenolic epoxy resin coating on KH550-modified SrAl2O4: Eu2+, Dy3+ powder in the presence of triarylsulfonium hexafluoroantimonate Type de document : texte imprimé Auteurs : Jing Li, Auteur ; Mingqiao Ge, Auteur ; Yanan Zhu, Auteur ; Zhi Chen, Auteur Année de publication : 2016 Article en page(s) : p. 1075-1082 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Copolymère phénolique époxy Epoxydes Phénoplastes Phosphore Photoluminescence Poudres Triarylsulfonium hexafluoroantimonate Index. décimale : 667.9 Revêtements et enduits Résumé : In this study, the amino silane coupling agent (KH550)-modified SrAl204: Eu2+, Dy3+ phosphor powder coated with phenolic epoxy resin (EOCN) in the presence of triarylsulfonium hexafluoroantimonate catalyst was prepared using the combination of organic–inorganic composite dip-coating and UV curing coating methods. The results of SEM, TEM, and FTIR showed that the organic coating was a layer of compact membrane with a thickness of 20–50 nm, which can be named silane-modified epoxy monomer generated by the KH550 and the EOCN. Furthermore, it was observed that afterglow and spectrum properties of the coated phosphor powder had good long-afterglow luminescence properties, and revealed two emission peaks at 435 nm and 520 nm under the same excitation wavelength of 360 nm, respectively. More interesting, the emitting color of the coated sample was located in the area of cyan light on CIE1931 chromaticity diagram, which led to a slight blue shift rather than the yellow–green color of the pure SrAl204: Eu2+, Dy3+ phosphor powder. Note de contenu : - EXPERIMENTAL METHODS AND MATERIALS : Materials - Synthesis of SrAl2O4: Eu2+, Dy3+ phosphor powder - Coating procedure - Photochemical reactions - Characterization - RESULTS AND DISCUSSION : Surface morphology analysis - FTIR spectroscopy analysis - Afterglow decay properties - PL characteristics - Photochromic properties DOI : 10.1007/s11998-016-9826-0 En ligne : http://link.springer.com/content/pdf/10.1007%2Fs11998-016-9826-0.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=27265 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
18514	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)