Preparation of HMDS-modified silica/polyacrylate hydrophobic hard coatings on PMMA substrates / Chao-Ching Chang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 13, N° 6 (11/2016)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 13, N° 6 (11/2016) . - p. 999-1007 Titre : Preparation of HMDS-modified silica/polyacrylate hydrophobic hard coatings on PMMA substrates Type de document : texte imprimé Auteurs : Chao-Ching Chang, Auteur ; Yu-Ting Wu, Auteur ; Liao-Ping Cheng, Auteur Année de publication : 2016 Article en page(s) : p. 999-1007 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Hydrophobie Matériaux hybrides Nanoparticules Polyacrylates Polyméthacrylate de méthyle Le poly(méthacrylate de méthyle) (souvent abrégé en PMMA, de l'anglais Poly(methyl methacrylate)) est un polymère thermoplastique transparent obtenu par polyaddition dont le monomère est le méthacrylate de méthyle (MMA). Ce polymère est plus connu sous son premier nom commercial de Plexiglas (nom déposé), même si le leader global du PMMA est Altuglas International9 du groupe Arkema, sous le nom commercial Altuglas. Il est également vendu sous les noms commerciaux Lucite, Crystalite, Perspex ou Nudec. Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Transparence (optique) Index. décimale : 667.9 Revêtements et enduits Résumé : Colloidal silica nanoparticles synthesized from tetraethoxysiliane via a sol–gel process were surface modified by 3-(trimethoxysilyl)propyl methacrylate (MSMA) and 1,1,1,3,3,3-hexamethyldisilazane (HMDS). MSMA acted both as a C=C provider and a coupling agent, whereas HMDS was used to prevent particle aggregation and engender hydrophobicity. The modified silica particles (HMSiO2) were UV-cured together with the crosslinking agent, dipentaerythritol hexa-acrylate (DPHA) to form coatings on poly(methyl methacrylate) (PMMA) substrates. Dynamic light scattering of the synthesized sols indicated that the average size of HMSiO2 was ca. 10 nm, consistent with that obtained from TEM imaging. FTIR spectroscopic analyses demonstrated chemical attachment of HMDS to the silica particles. The cured coatings were characterized in terms of water contact angle, light transmittance, hardness, abrasion resistance, and surface morphology. It was found that hydrophobicity of the coatings increased while light transmittance and hardness decreased with increasing HMDS content. DPHA played the role of providing mechanical strength and adherence; however, the coatings became lightly hazy when the weight ratio of DPHA/silica fell in the range 0.3–0.7. In the optimal case, a hard coating (4H) with water contact angle of 108° and transmittance of ~100% (vs PMMA) had been obtained at the DPHA content of 10 wt%. Note de contenu : - EXPERIMENTAL : Materials - Preparation of surface-modified silica particles - Preparation of silica/polyacrylate coatings - Characterization - RESULTS AND DISCUSSION : Analyses of the HMSiO2 sols - Properties of the coatings DOI : 10.1007/s11998-016-9820-6 En ligne : http://link.springer.com/content/pdf/10.1007%2Fs11998-016-9820-6.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=27253 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
18514	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)