Fabrication of fine microcapsulated red phosphorus particles by SCF-RESS with a new structure nozzle |
| Type de document : |
texte imprimé |
| Auteurs : |
Ya-qing Liu, Auteur ; Fa-Xing Zhang, Auteur ; You-yi Sun, Auteur ; Gui-zhe Zhao, Auteur |
| Année de publication : |
2008 |
| Article en page(s) : |
p. 465-471 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Dioxyde de carbone
Encapsulation
Fluides supercritiques
Microcapsules
Phosphore
Rouge (couleur)
|
| Index. décimale : |
660.2 Génie chimique |
| Résumé : |
A novel process of preparing microencapsulated red phosphorus particles by rapid expansion of supercritical fluids (RESS) was tested, in which a new kind of nozzle and supercritical CO2 as a solvent were used. The structure of the microencapsulated red phosphorus particles were characterized by scanning electron microscope (SEM) and transmission electron microscope (TEM). These results show that red phosphorus particles can be effectively encapsulated with paraffin by using the method. At the same time, how the moisture absorption ratio of microencapsulated red phosphorus particles was dependent on the experimental conditions was further investigated. The results suggest that paraffin-microencapsulated red phosphorus particles show a lower moisture absorption ratio within the experimental conditions of the extraction column and nozzle temperature of 120°C, extraction column pressure of more than 16 MPa, and a mass flow of core particles (0.5 g/min). |
| DOI : |
10.1007/s11998-008-9091-y |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-008-9091-y.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=3472 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 5, N° 4 (12/2008) . - p. 465-471