Synthesis of conducting PANi/SiO2 nanocomposites and their effect on electrical and mechanical properties of antistatic waterborne epoxy coating |
| Type de document : |
texte imprimé |
| Auteurs : |
Anh Son Nguyen, Auteur ; Thuy Duong Nguyen, Auteur ; Thu Thuy Thai, Auteur ; Anh Truc Trinh, Auteur ; Gia Vu Pham, Auteur ; Hoang Thai, Auteur ; Dai Lam Tran, Auteur ; Thi Xuan Hang To, Auteur ; Duy Trinh Nguyen, Auteur |
| Année de publication : |
2020 |
| Article en page(s) : |
p. 361-370 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Antistatiques
Dioxyde de silicium
Epoxydes
Matériaux hybrides
Polyaniline
Polymères -- Propriétés électriques
Polymères en émulsion
Revêtements -- Propriétés mécaniques
Revêtements en phase aqueuse -- Additifs
Revêtements organiques
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Polyaniline (PANi) has been intensively incorporated in epoxy coatings as a conducting material. However, epoxy coatings containing PANi have poor mechanical properties. In this study, polyaniline/silica (PANi/SiO2) nanocomposites with different contents of silica were prepared via in situ chemical oxidative polymerization method. Fourier transform infrared spectroscopy (FTIR), field emission scanning electron microscopy (FESEM), and zeta potential measurements were used to examine the structure and the morphology of synthesized PANi/SiO2 nanocomposites. The thermal and electrical properties of the nanocomposite were studied by thermogravimetric analysis (TGA) and standard four-probe electrode method. It was shown that silica (SiO2) nanoparticles were covered by PANi in PANi/SiO2 nanocomposites and the electrical conductivity of nanocomposites decreased with the increase in SiO2 content. The PANi/SiO2 nanocomposite with 4.1 wt% SiO2 had a conductivity of 7.6 x 10-2 S/cm and that of PANi was 8.7 x 10-2 S/cm. Consequently, epoxy coatings containing 30 wt% PANi/SiO2 nanocomposites displayed a higher surface and volume resistance than the one containing pure PANi. In contrast, the increase in SiO2 content in PANi/SiO2 nanocomposite enhanced the mechanical properties of the epoxy coating, compared to epoxy coating containing pure PANi. The coating containing PANi/SiO2 nanocomposite with 17.2 wt% silica presented good mechanical properties (20 L/mil abrasion resistance, 100 kg cm impact strength) and admissible surface and volume resistivity (1.3 x 1011 Ω/cm2 and 6.6 x 10 10 Ω cm, respectively) for antistatic coatings. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Preparation of PANi/Sio2 nanocomposites - Preparation of Coatings - Analytical characterization - Conductivity measurement - Mechanical resistance measurement
- RESULTS AND DISCUSSION : Characterization of PANi/SiO2 nanocomposite |
| En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-019-00279-2.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33987 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 17, N° 2 (03/2020) . - p. 361-370
Aller sur edunet
Accueil
Synthesis of conducting PANi/SiO2 nanocomposites and their effect on electrical and mechanical properties of antistatic waterborne epoxy coating in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 17, N° 2 (03/2020)