| Titre : |
Comparative analysis of structural properties of PET POY and DTY |
| Type de document : |
texte imprimé |
| Auteurs : |
Yash Marathe, Auteur ; Ranjit Turukmane, Auteur |
| Année de publication : |
2019 |
| Article en page(s) : |
p. 94-96 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Etudes comparatives
Fibres textiles -- Propriétés mécaniques
Fil a texture étiré
Fil partiellement orienté
FilamentsFibre de longueur infinie ou extrême comme celle qu'on trouve dans la soie à l'état naturel. Les fibres manufacturées sont extrudées en filaments qui sont transformés en fils continus, en fibres courtes ou en câbles.
Polyéthylène téréphtalate
|
| Index. décimale : |
677.4 Textiles artificiels |
| Résumé : |
Structural properties of PET filament largely depend on the several factors such as yarn types, filament, fineness and shapes etc. which are the detrimental factors considered for the extent of deformations. The draw ratio, heater temperature and post spinning operations decide the nature of the filament and its applicability. This work was carried out to determine the structural difference between partially oriented yarns (POY) and draw-textured yarns (DTY). For both the types, PET was considered to be the base material. The manufactured POY package was processed on draw-textured machine with standard settings, processed POY denier was 160/144 and it was observed for the testing of tenacity, elongation and boiling water shrinkage. Favorable transformation of cheaper and stronger flat filament feeder yarn structure to favorable crimpy/bulky yarn structure was an added gain of this production process. All the samples also showed good crimp associated properties. Thus newly designed draw-textured fancy yarn will add considerable value along with added comfort to apparel textiles as well as home furnishing. |
| Note de contenu : |
- Table 1 : Different shades PET POY
- Table 2 : Comparative analysis of tenacity for PC6B0118T POY and tex package
- Table 3 : Comparative analysis of elongation for PC6B0118T POY and tex package
- Table 4 : Comparative analysis of boiling water shrinkage for PC6B0118T POY and tex package
- Table 5 : Comparative analysis of tenacity for PC7A1105T POY and tex package
- Table 6 : Comparative analysis of elongation for PC7A1105T POY and tex package
- Table 7 : Comparative analysis of boiling water shrinkage (BWS) for PC7A1105T POY and tex package
- Table 8 : Comparative analysis of tenacity for PC6B0107T POY and tex package
- Table 9 : Comparative analysis of elongation for PCB0107 (corydalis blue) POY and tex package
- Table 10 : Comparative analysis of boiling water shrinkage for PC6B0107T (corydalis blue) POY and tex package |
| En ligne : |
https://drive.google.com/file/d/1MMZbqXffyHjDAWJHIuDbsT8XWo_1EdG7/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=32775 |
in CHEMICAL FIBERS INTERNATIONAL > Vol. 69, N° 2 (06/2019) . - p. 94-96
Aller sur edunet