Facile synthesis of epoxy nanocomposite coatings using inorganic nanoparticles for enhanced thermo-mechanical properties : a comparative study / Rawaiz Khan in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 13, N° 1 (01/2016)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 13, N° 1 (01/2016) . - p. 159-169 Titre : Facile synthesis of epoxy nanocomposite coatings using inorganic nanoparticles for enhanced thermo-mechanical properties : a comparative study Type de document : texte imprimé Auteurs : Rawaiz Khan, Auteur ; Muhammad Rizwan Azhar, Auteur ; Arfat Anis, Auteur ; Mohammad Asif Alam, Auteur ; M. Boumaza, Auteur ; Saeed M. Al-Zahrani, Auteur Année de publication : 2016 Article en page(s) : p. 159-169 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Dioxyde de silicium Epoxydes Matériaux hybrides Nanoindentation Nanoparticules Oxyde de fer Oxyde de zinc Revêtements -- Propriétés mécaniques Revêtements -- Propriétés thermiques Zircone Le dioxyde de zirconium ou oxyde de zirconium(IV) couramment appelée zircone est un composé inorganique du zirconium de formule ZrO2. Ce matériau est une céramique technique d'aspect opaque. Appelé CZ (Cubic Zirconia) lorsque transparent, il est utilisé pour imiter le diamant. Il ne faut pas le confondre avec le zircon (ZrSiO4). Sous sa forme tétragonale, l'oxyde de zirconium est un matériau a vocation mécanique, cette évolution cristallographique lui confère une dureté très élevée (1200Hv) ainsi qu'une bonne résistance aux sollicitations mécaniques (700Mpa en traction et 2000Mpa en compression). Une fois polie, la zircone tétragonale peut atteindre un Ra de 0,02, ce qui permet de l'utiliser pour des pièces de frottement. Index. décimale : 668.5 Parfums et cosmétiques Résumé : Epoxy-based nanocomposite coatings were formulated by incorporating various types of inorganic nanoparticles (NPs) (ZrO2, ZnO, Fe2O3, and SiO2). The effect of the incorporation of various NPs on the mechanical, thermal, and morphological properties of these epoxy coatings has been studied. A facile direct incorporation technique has been utilized for the dispersion of the NPs in the epoxy matrix via high-speed mechanical stirring and ultra-sonication using acetone as a solvent. The incorporation of these NPs augmented the mechanical and thermal properties of the epoxy coatings. The results revealed that the incorporation of small amount of these NPs improved the mechanical properties of the coating in all cases, with the SiO2-reinforced sample being relatively better in both mechanical and thermal properties. The incorporation of Fe2O3 and ZnO resulted in a decrease in the thermal stability and glass transition temperature (T g) of the coatings, while incorporation of SiO2 and ZrO2 increased the thermal stability as well as T g of the coatings. A notable increase of 71% in hardness together with 26% increase in the elastic modulus of the epoxy coating was observed with the incorporation of 2 wt% SiO2 NPs. Note de contenu : - EXPERIMENTAL : Materials - Sample preparation - CHARACTERIZATION - RESULTS AND DISCUSSION : Miscrostructure characterization - Fourier transform infrared spectroscopy and X-ray diffraction analysis - Mechanical properties - Thermal properties DOI : 10.1007/s11998-015-9736-6 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-015-9736-6.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25385 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
17819	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)