Enhancing flame retardancy, thermal stability, physical and mechanical properties of polyethylene foam with polyphosphate modified expandable graphite and ammonium polyphosphate |
| Type de document : |
texte imprimé |
| Auteurs : |
M.-F. Ma, Auteur ; Xiaoyan Pang, Auteur ; R. Chang, Auteur |
| Année de publication : |
2019 |
| Article en page(s) : |
p. 239-247 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Graphite
IgnifugeantsComposé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface.
Mousses plastiques
Mousses plastiques -- Propriétés mécaniques
Mousses plastiques -- Propriétés physiques
Mousses plastiques -- Propriétés thermiques
Polyéthylène basse densité linéaire
Polyphosphate d'ammonium
PolyphosphateUn polyphosphate est un sel ou un ester d'oxyanions polymères formés à partir d'unités structurales tétraédriques PO 4 (phosphate) liées entre elles par le partage d'atomes d'oxygène. Les polyphosphates peuvent adopter des structures cycliques linéaires ou cycliques. En biologie, les esters polyphosphates ADP et ATP sont impliqués dans le stockage de l'énergie. Une variété de polyphosphates trouvent une application dans la séquestration des minéraux dans les eaux municipales, étant généralement présents à 1 à 5 ppm. GTP, CTP et UTP sont également des nucléotides importants dans la synthèse des protéines, la synthèse des lipides et le métabolisme des glucides, respectivement. Les polyphosphates sont également utilisés comme additifs alimentaires, marqués E452. (Wikipedia)
|
| Index. décimale : |
668.4 Plastiques, vinyles |
| Résumé : |
The method of preparing polyolefin foam with good flame retardancy, thermal stability, and physical and mechanical properties was investigated. Foaming condition of linear low density polyethylene (LLDPE) was investigated with triphenyl phosphate (TPP) as plasticizer, NaHCO3 as foaming agent. The influence of modified expandable graphite (EGP) and ammonium polyphosphate (II) on foam density, compression strength, combustion characteristics and thermal stability was explored. Results verified that EGP presented better dilatability and flame retardancy than the normal expandable graphite. Addition of EGp improved the limiting oxygen index (LOI) of 15NaHCO3/100 LLDPETPP/30EGp foam from 18.8% to 24.6%. Furthermore, the combination of EGp and ammonium polyphosphate (II) (APP) at the mass ratio of 2:1 improved the LOI of 15NaHCO3/100 LLDPETPP/20EGp/10APP sample to 27.9%, and the vertical burning UL-94 level reached V-0, indicating that this material was flame retardant. Although these additives made 15NaHCO3/100 LLDPETPP/20EGp/10APP composite exhibit a high density of 142.5 kg m−3, which was increased by 12.3 wt% relative to the 15NaHCO3/100 LLDPETPP foam, it could improve the compressive strength to 0.4747 MPa, which was about 2.7 times that of the matrix. The thermal stability of the material was also enhanced. |
| Note de contenu : |
- EXPERIMENTAL PROCEDURE : Raw materials - Sample preparation - Measurement and characterization of different properties
- RESULTS AND DISCUSSION : TG/DTG analysis of the prepared GICs - Influence of FRs on physical and mechanical properties of LLDPE foam - Influence of FRs on LLDPE foams combustion properties - Combustion residue morphology - Influence of FRs on LLDPE foams thermal stability - Possible flame retardant mechanism |
| DOI : |
10.3139/217.3714 |
| En ligne : |
https://drive.google.com/file/d/1Bmrx4Qqz6pEqk72LCifUoz3HT62hiej1/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=32398 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XXXIV, N° 2 (05/2019) . - p. 239-247
[article]
|
Aller sur edunet
Accueil
Enhancing flame retardancy, thermal stability, physical and mechanical properties of polyethylene foam with polyphosphate modified expandable graphite and ammonium polyphosphate in INTERNATIONAL POLYMER PROCESSING, Vol. XXXIV, N° 2 (05/2019)