Crystallization behavior and mechanical properties of nanosilica-reinforced isotactic polypropylene composites / J. Li in INTERNATIONAL POLYMER PROCESSING, Vol. XXX, N° 5 (11/2015)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXX, N° 5 (11/2015) . - p. 542-547 Titre : Crystallization behavior and mechanical properties of nanosilica-reinforced isotactic polypropylene composites Type de document : texte imprimé Auteurs : J. Li, Auteur ; L.-J. Long, Auteur ; W.-T. He, Auteur ; K. Zhang, Auteur ; Y.-S. Xiang, Auteur ; J. Zhang, Auteur ; M.-M. Zhang, Auteur ; C.-P. Yang, Auteur ; J. Yu, Auteur Année de publication : 2015 Article en page(s) : p. 542-547 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caractérisation Charges (matériaux) Flexion (mécanique) Gel de silice Nanoparticules Polymères -- Propriétés mécaniques Polymères isotactiques Polypropylène Résistance au chocs Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Structure cristalline (solide) Traction (mécanique) Index. décimale : 668.9 Polymères Résumé : Two different types of inorganic silica fillers, nano-silica powder (NSP) and colloidal silica sol (CSS) were added into isotactic polypropylene (iPP) with low silica content (0.2 wt%) and the influence of the two silica fillers on the crystallization behavior and mechanical properties of iPP were investigated. Differential scanning calorimeter (DSC) results showed that the crystallization temperature of iPP with CSS and NSP were increased by 4.1 °C, and 2.4 °C, respectively. The tensile strength, flexural strength, and izod impact strength of iPP/CSS (33.75 MPa, 33.04 MPa, and 4.80 kJ/m2) were higher than that of iPP/NSP (32.09 MPa, 32.27 MPa, and 4.25 kJ/m2). In addition, the haze value of iPP/CSS was decreased from 37.6 % to 27.6 %, which was 4.7 % lower than that of iPP/NSP (32.3 %). The better performance of CSS as ascribed to its better dispersion ability in iPP matrix than NSP, and it was verified by scanning electron micrograph (SEM) and transmission electron microscope (TEM). Overall, these results indicated that inorganic silica sols had a potential application in the nanoparticle-reinforced composites field. Note de contenu : - EXPERIMENTAL : Raw materials - Preparation of iPP/silica composites - Characterization - RESULT AND DISCUSSION : Crystalline structure and crystallization behavior DOI : 10.3139/217.3065 En ligne : https://drive.google.com/file/d/1TckKt9TRURlEoVI-WZbYRc0LDIc3Gqeg/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=24815 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
17557	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)