A simple method to make mechanically robust, adhesive and superhydrophobic surface based on epoxy resin / Aoyun Zhuang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 12, N° 3 (05/2015)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 12, N° 3 (05/2015) . - p. 609-615 Titre : A simple method to make mechanically robust, adhesive and superhydrophobic surface based on epoxy resin Type de document : texte imprimé Auteurs : Aoyun Zhuang, Auteur ; Lijun Yang, Auteur ; Ruijin Liao, Auteur ; Chao Guo, Auteur ; Zhiping Zuo, Auteur ; Yuan Yuan, Auteur Année de publication : 2015 Article en page(s) : p. 609-615 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Abrasion Adhésifs -- Propriétés mécaniques Bisphénol A Caractérisation Colles:Adhésifs Epoxydes Essais dynamiques Hydrophobie Nanoparticules Résistance chimique Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Verre -- Collage Index. décimale : 667.9 Revêtements et enduits Résumé : A robust micro/nano-structured superhydrophobic surface was facilely prepared by applying composite coating consisting of epoxy resin and silica nanoparticles on glass substrates. The whole process only needed bisphenol A-based epoxy resin and silica nanoparticles to be mixed, coated, and dried. Field emission scanning electron microscopy, atomic force microscopy, and a drop meter were utilized to evaluate its morphology, accurate topography, quantitative roughness, and wettability, respectively. After considering adhesive force and the superhydrophobicity of the coating, it was shown that the best result was gained when the solid content of the silica nanoparticles was 45.5 wt%. In addition, the coating showed excellent surface mechanical stability and acid-alkali resistance which offers great potential for durable application in various fields. Note de contenu : - EXPERIMENT : Materials - Preparation of superhydrophobic epoxy resin surface - Characterization of samples - RESULTS AND DISCUSSION : Superhydrophobic surfaces from bisphenol A epoxy with silica nanoparticles - Abrasion test for robust structure - Test of acid-alkali resistance of superhydrophobic surfaces DOI : 10.1007/s11998-014-9653-0 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-014-9653-0.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=24185 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
17244	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)