Titre : |
Study on a novel composite coating based on PDMS doped with modified graphene oxide |
Type de document : |
texte imprimé |
Auteurs : |
Jijun Tang, Auteur ; Wei Yao, Auteur ; Weili Li, Auteur ; Jie Xu, Auteur ; Lei Jin, Auteur ; Jide Zhang, Auteur ; Zexiao Xu, Auteur |
Année de publication : |
2018 |
Article en page(s) : |
p. 375-383 |
Note générale : |
Bibliogr. |
Langues : |
Américain (ame) |
Catégories : |
Anticorrosion Composites Dispersions et suspensions Essais de résilience Oxyde de graphène PolydiméthylsiloxaneLe polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones.
Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone.
Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK).
La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Réaction de couplage Réticulants Revêtements Revêtements -- Propriétés mécaniques:Peinture -- Propriétés mécaniques Revêtements:Peinture Silanes Sol-gel, Procédé Tétraéthoxysilane Thermocinétique
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
The low surface activity of graphene oxide (GO) stemming from its large conjugated electronic structure can easily affect the dispersion behavior of GO-based polymer matrices. This significantly undermines the properties of the resulting composite materials. Therefore, in order to increase the GO surface activity for use in polymer-based composites, GO was modified using silane coupling agent which was then doped into polydimethylsiloxane (PDMS) polymer to prepare novel paints by sol–gel reaction strategy. The subsequent novel composite coatings based on PDMS/modified GO (mGO) were finally cured with tetraethoxysilane as the hardening agent in the presence of dibutyltin dilaurate catalyst. The effect of doping mGO into PDMS polymer was systematically studied using infrared spectroscopy, micro-Raman spectroscopy, TEM, SEM, XRD, TGA, mechanical test, thermal conductivity test, and the erosion resistance test. It was concluded that the phase compatibility between GO and PDMS was enhanced due to the new interconnecting chemical bonds brought about by the mGO in the composite. |
Note de contenu : |
- EXPERIMENTAL : Materials - Preparations of graphene oxide and chlorination of graphene oxide - Preparation of composite coatings - Characterization
- RESULTS AND DISCUSSION : Materials characterization - Morphological analysis - Thermal stability property - Mechanical properties - Thermal conductivity - Anticorrosion property |
DOI : |
10.1007/s11998-017-9991-9 |
En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-017-9991-9.pdf |
Format de la ressource électronique : |
pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30296 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 2 (03/2018) . - p. 375-383