| Titre : |
The effect of MIO pigments on corrosion resistance and adhesion of synthetic rubber-based primer |
| Type de document : |
texte imprimé |
| Auteurs : |
Hojatollah Erfaghi, Auteur ; Mansour Farzam, Auteur ; Davood Zaarei, Auteur ; Iman Danaee, Auteur |
| Année de publication : |
2018 |
| Article en page(s) : |
p. 351-362 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Acier au carbone
Anticorrosion
Corrosion
Essais d'adhésion
Essais de résilience
Essais dynamiques
Métaux -- Revêtements protecteurs
Microscopie électronique à balayage
Oxyde de fer micacé
Pipelines -- Revêtements protecteurs
Spectroscopie d'impédance électrochimique
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
In this research, the corrosion resistance and adhesion property of a synthetic rubber-based primer reinforced with different ratios of micaceous iron oxide (MIO) pigments were studied. Coatings were applied on carbon steel panels and also on steel pipes of 219.1 mm outer diameter. Scanning electron microscopy (SEM) was used to investigate the dispersion of MIO particles in the rubbery matrix. The anticorrosion performance of the coatings was studied, using electrochemical impedance spectroscopy (EIS) and salt spray tests. In addition, the adhesion of primers to carbon steel substrates was evaluated by pull-off test. In order to investigate the effect of MIO particles on the flexibility of the pigmented primers, a cupping test was conducted. The adhesion of cold-applied tape to the formulated primers was assessed by peel adhesion test using hanging mass method. The results indicated that adding 5, 10, and 15 wt% of MIO pigments into the primer improved corrosion resistance of the coatings. An increase in the MIO loading up to 10 wt%, improved the adhesion of the primer to both steel substrate and cold-applied tape. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Preparation of coatings
- LABORATORY TESTS : Corrosion behavior - Adhesion tests - Cupping test
- RESULTS AND DISCUSSION : SEM analysis - EIS results - Salt spray test results - Pull-off adhesion results - Peel adhesion results - Cupping test results |
| DOI : |
10.1007/s11998-017-9987-5 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-017-9987-5.pdf |
| Format de la ressource électronique : |
pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30294 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 2 (03/2018) . - p. 351-362
Aller sur edunet
Accueil
The effect of MIO pigments on corrosion resistance and adhesion of synthetic rubber-based primer in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 2 (03/2018)