| Titre : |
PVDF/graphene oxide composite nanofibers |
| Type de document : |
texte imprimé |
| Auteurs : |
Hong Yan Wu, Auteur |
| Année de publication : |
2018 |
| Article en page(s) : |
p. 208-210 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Composites
Electrofilature
Mesure
Microscopie électronique à balayage
Morphologie (matériaux)
Nanofibres
Oxyde de graphène
Polyfluorure de vinylidène
|
| Index. décimale : |
677.4 Textiles artificiels |
| Résumé : |
By electrospinning method, graphene oxide (GO) was used to prepared a series of polyvinylene fluoride (PVDF) PVDF/GO composite nanofibers with different mass fraction of GO. The microstructure of the composite nanofibers was observed using the scanning electron microscope (SEM), and the mean fiber diameter and standard deviation were calculated. The results show that when the mass fraction of GO is high, the PVDF/GO composite nanofibers cannot be prepared. When GO was added, the roughness of the fiber surface is obviously increased,the appearance is uneven, and small holes and raised particles appear in the fiber surface. With the increase of the quality of GO, the average diameter of the fiber increases, and the standard deviation has no obvious change regulation. |
| Note de contenu : |
- EXPERIMENTS : Matérials, reagents and instruments - Preparation of PVDF/GO composite nanofibers - Property of PVDF/GO composite nanofibers
- RESULTS AND DISCUSSIONS : Macroscopic morphology of composite nanofibers - Microscopic morphology of composite nanofibers
- Diameter of composite nanofibers |
| En ligne : |
https://drive.google.com/file/d/1bTBknrodQjaHwYYs0nY7ui9nshx1BgxP/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=29723 |
in CHEMICAL FIBERS INTERNATIONAL > Vol. 67, N° 4 (12/2017) . - p. 208-210
Aller sur edunet
Accueil
PVDF/graphene oxide composite nanofibers in CHEMICAL FIBERS INTERNATIONAL, Vol. 67, N° 4 (12/2017)