The effect of thermal radical initiator derived from O-imino-isourea on thermal curing characteristics and properties of automotive clearcoats / Ji Won Hwang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 12, N° 1 (01/2015)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 12, N° 1 (01/2015) . - p. 177-186 Titre : The effect of thermal radical initiator derived from O-imino-isourea on thermal curing characteristics and properties of automotive clearcoats Type de document : texte imprimé Auteurs : Ji Won Hwang, Auteur ; Kyung Nam Kim, Auteur ; Seung Man Noh, Auteur ; Hyun Wook Jung, Auteur Année de publication : 2015 Article en page(s) : p. 177-186 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Amorceurs (chimie) Automobiles -- Vernis Hydroxyle En chimie organique, un hydroxyle (ou oxhydryle) peut désigner deux entités. Un groupement -OH, appelé aussi hydroxy, qui se rencontre en particulier dans les alcools et les phénols. Un radical : HO^{\bullet}. Il est produit par exemple lors de réactions de dissociation de peroxydes, en présence d'ions de métaux de transition (Fe(II), Cu(I), réaction de Fenton), de chauffage ou de rayonnement. Mélamine La mélamine, de nom chimique 1,3,5-triazine-2,4,6-triamine, est parfois dénommée cyanuramide ou cyanurotriamine. Sa formule brute est C3H6N6. Les "résines mélamine-formaldéhyde" ou "mélamine-formol" (sigle MF) sont appelées "mélamine" dans le langage courant. Elles font partie de la famille des aminoplastes qui regroupe des résines thermodurcissables aminées, issues d'un comonomère tel l'urée ou la mélamine, parfois le thiocarbamide, le cyanamide hydrogène ou le dicyandiamide ; le second comonomère étant le formaldéhyde. Méthacrylate d'uréthane Oligomères Polyaddition Résistance à l'abrasion Réticulation (polymérisation) Rhéologie Vernis -- Propriétés mécaniques Index. décimale : 667.9 Revêtements et enduits Résumé : Curing characteristics of melamine-based automotive clearcoats with or without thermal radical initiator (TRI) derived from an O-imino-isourea have been examined by means of their real-time rheological properties during a thermal curing process. By changing functionalities of reactive sites at hydroxyl groups and unsaturated double bonds in hydroxyl-functionalized urethane methacrylate oligomer as a main binder, the effect of TRI on various properties of thermally cured clearcoats has been compared by means of rheological, rigid-body pendulum, ultra nano-indentation, and nano-scratch tests. It was found that a small portion of TRI significantly enhanced the final elastic modulus of clearcoats with the lower content of hydroxyl groups and considerably shortened curing time, implying the formation of denser crosslinked networks inside clearcoats by the free-radical polymerization at relatively lower curing temperature. These results were directly linked with the improvement of their mechanical properties such as indentation hardness and scratch resistance. TRI plays a key role in desirably controlling the rheological and mechanical properties of clearcoats under insufficient thermal curing conditions. Note de contenu : - EXPERIMENTAL : Preparation of clearcoat samples - Characterization methods - RESULTS AND DISCUSSION : Thermal characteristics of clearcoats - Comparison of elastic rheological data for clearcoats with or without TRI - Curing characteristics by RPT tests - Mechanical properties of cured clearcoats DOI : 10.1007/s11998-014-9619-2 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-014-9619-2.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=23216 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16952	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)