The effect of zirconia ions on corrosion performance of sol–gel coated galvanized steel / Akshya Kumar Guin in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 6 (11/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 6 (11/2014) . - p. 967-977 Titre : The effect of zirconia ions on corrosion performance of sol–gel coated galvanized steel Type de document : texte imprimé Auteurs : Akshya Kumar Guin, Auteur ; Manish Bhadu, Auteur ; Mohua Sinhababu, Auteur ; G. Udayabhanu, Auteur Année de publication : 2014 Article en page(s) : p. 967-977 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosion Essais de brouillard salin Polarisation (électricité) Polymères Sol-gel, Procédé Spectroscopie d'impédance électrochimique Zircone Le dioxyde de zirconium ou oxyde de zirconium(IV) couramment appelée zircone est un composé inorganique du zirconium de formule ZrO2. Ce matériau est une céramique technique d'aspect opaque. Appelé CZ (Cubic Zirconia) lorsque transparent, il est utilisé pour imiter le diamant. Il ne faut pas le confondre avec le zircon (ZrSiO4). Sous sa forme tétragonale, l'oxyde de zirconium est un matériau a vocation mécanique, cette évolution cristallographique lui confère une dureté très élevée (1200Hv) ainsi qu'une bonne résistance aux sollicitations mécaniques (700Mpa en traction et 2000Mpa en compression). Une fois polie, la zircone tétragonale peut atteindre un Ra de 0,02, ce qui permet de l'utiliser pour des pièces de frottement. Index. décimale : 667.9 Revêtements et enduits Résumé : Currently, galvanized steel is treated with hexavalent chrome passivation. Sol–gel coating has been found to be a potential replacement for the hazardous hexavalent chrome passivation treatment. The aim of this work is to study the effect of zirconyl nitrate on corrosion behavior of sol–gel coating. Aminopropyl-trimethoxysilane and 3-glycidoxypropyltrimethoxysilane were employed as precursors to prepare the sol–gel-based silane coating. The sol–gel film was deposited on galvanized steel sheet by dip coating method. The chemical properties of sol–gel solution and coated films were analyzed by infrared spectroscopy. Morphology of the film was characterized by scanning electron microscope. The corrosion resistance of the coated samples was evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization curve, and salt spray test. The results indicated that zirconia-doped coatings have better corrosion resistance in comparison with their undoped counterparts. The coating doped with 0.5% zirconyl nitrate provides better corrosion protection due to the inhibitive action of zirconia ion. Note de contenu : - EXPERIMENTAL : Materials and reagents - Preparation of coatings - Measurements - RESULTS AND DISCUSSION : FTIR analysis - SEM micrograph - Surface roughness - Salt spray study (ASTM B-117) - Polarization study - Electrochemical impedance (EIS) study DOI : 10.1007/s11998-014-9602-y En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-014-9602-y.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=22319 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16659	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)