Synthesis of hollow α-Fe2O3–silica composites templated by poly(acrylic acid) colloidal aggregates / Dan Liu in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 4 (07/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 4 (07/2014) . - p. 595-600 Titre : Synthesis of hollow α-Fe2O3–silica composites templated by poly(acrylic acid) colloidal aggregates Type de document : texte imprimé Auteurs : Dan Liu, Auteur ; Ziheng Li, Auteur ; Gen Li, Auteur ; Fei Wang, Auteur ; Wenquan Wang, Auteur Année de publication : 2014 Article en page(s) : p. 595-600 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Composites Frittage Le frittage est un procédé de fabrication de pièces consistant à chauffer une poudre sans la mener jusqu’à la fusion. Sous l'effet de la chaleur, les grains se soudent entre eux, ce qui forme la cohésion de la pièce. Hématite Matériaux mésoporeux Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Index. décimale : 667.9 Revêtements et enduits Résumé : The synthesis of inorganic hollow nanoparticles has attracted more and more attention in recent research. In this article, hollow α-Fe2O3–silica composites were synthesized by a modified Stöber method. Tetraethyl orthosilicate (TEOS) formed oil drops, and ammonia solution facilitated the hydrolysis polymerization of TEOS. In the hydrolysis process of TEOS, we used cetyltrimethylammonium bromide and poly(acrylic acid) colloidal aggregates as the surfactant and template, respectively. The diameters of the composites we obtained are about 20 and 180 nm, respectively, which are smaller than that of pure silica spheres (200 nm). Moreover, Brunauer–Emmett–Teller surface areas of hollow α-Fe2O3–silica composites were determined to be in the range of 377–498 m2/g, and their pore sizes are around 2 nm as were determined by BJH method. The mesoporous silica was successfully coated around the α-Fe2O3. The synthesis process of the composites is a simple, one-step route, which exhibits the potential need for a great amount of synthesis for future research. Note de contenu : - EXPERIMENTAL PROCEDURE : Materials - Synthesis of α-Fe2O3–silica composites - Characterization - RESULTS AND DISCUSSION : XRD analysis of α-Fe2O3–silica composites - SEM image of α-Fe2O3–silica composites - Nitrogen adsorption-desorption isotherms and pore size distribution - The formation mechanism of α-Fe2O3–silica composites DOI : 10.1007/s11998-014-9569-8 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-014-9569-8.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21720 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16424	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)