Preparation and characterization of transparent fluorocarbon emulsion doped with antimony tin oxide and TiO2 as thermal-insulating and self-cleaning coating / Xiande Lu in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 4 (07/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 4 (07/2014) . - p. 567-574 Titre : Preparation and characterization of transparent fluorocarbon emulsion doped with antimony tin oxide and TiO2 as thermal-insulating and self-cleaning coating Type de document : texte imprimé Auteurs : Xiande Lu, Auteur ; Gang Yu, Auteur ; Quan Tan, Auteur ; Bonian Hu, Auteur ; Jun Zhang, Auteur ; Qizhi Dong, Auteur Année de publication : 2014 Article en page(s) : p. 567-574 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Dioxyde d'étain Dioxyde de titane Hydrocarbures fluorés Isolation thermique Nanoparticules Oxydes d'antimoine Le trioxyde d’antimoine, également appelé trioxyde de diantimoine ou oxyde d’antimoine(III), est un composé inorganique de formule Sb2O3. Il s’agit d’un oxyde d'antimoine se présentant au laboratoire sous la forme d’une poudre blanche, sa forme minérale étant la sénarmontite (cristaux cubiques incolores) ou la valentinite (cristaux orthorhombiques blancs). La sénarmontite, stable à température ordinaire, se transforme à 570 °C en valentinite, métastable en dessous de cette température. - Écotoxicologie : En 2022, alors que les mécanismes de toxicité aquatique du Sb sont encore très mal compris, celle de la toxicité moléculaire du Sb(III) l'est plus encore, mais fait l'objet de quelques étude - Utilisations : Il est utilisé comme agent de synergie avec des composés halogénés pour l'ignifugation5 des polymères et textiles ; opacifiant pour verres, céramiques et émaux ; pigment pour peintures et catalyseur chimique. Revêtement auto-nettoyant Revêtements en phase aqueuse Revêtements protecteurs Transparence (optique) Verre -- Revêtements Index. décimale : 667.9 Revêtements et enduits Résumé : A transparent thermal insulation and self-cleaning coating was prepared from a fluorocarbon emulsion doped with antimony tin oxide (ATO) and anatase TiO2 nanoparticles. The thermal insulation and self-cleaning properties of the coating film were optimized by adjusting the amount of ATO and anatase TiO2 nanoparticles in the fluorocarbon emulsion. The fluorocarbon coating containing 2.0 wt% ATO and 0.1 wt% TiO2 possessed good comprehensive properties of thermal resistance, self-cleaning, weathering resistance, etc. Compared with the blank glass substrate, the mean light transmittance of the coating film only decreased by about 12% in the visible range. The temperature in the chamber covered with the coated glasses decreased 7°C lower than the common glass chamber without coating. The methyl red painted on the coating was completely faded after three days of ultraviolet irradiation, so the coating film exhibited an excellent self-cleaning property. The transparent coating with excellent thermal insulation and good self-cleaning will be developed for a potential building glass paint used for energy saving and environmental protection. Note de contenu : - EXPERIMENTAL DETAILS : Materials - Preparation of transparent fluorocarbon coating - Characterization of coating film - RESULTS AND DISCUSSION : The composition of coating film analysis - The transmittance of coating film analysis - The thermal insulation of coating film analysis - The self-cleaning properties of coating film analysis DOI : 10.1007/s11998-013-9550-y En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9550-y.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21717 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16424	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)