| Titre : |
The effects of tannins on adhesion strength and surface roughness of varnished wood after accelerated weathering |
| Type de document : |
texte imprimé |
| Auteurs : |
Mesut Yalcin, Auteur ; Hediye Ceylan, Auteur |
| Année de publication : |
2017 |
| Article en page(s) : |
p. 185-193 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Adhésion
Angle de contact
Bois -- Vernis
CelluloseLa cellulose est un glucide constitué d'une chaîne linéaire de molécules de D-Glucose (entre 200 et 14 000) et principal constituant des végétaux et en particulier de la paroi de leurs cellules.
Essais accélérés (technologie)
Mimosa et constituants
Polyuréthanes
QuebrachoLe quebracho est un arbre à écorce ligneuse, mesurant 30 mètres de haut, à feuilles tannées et à fleurs tubulées blanches.
Quebracho est l'un des noms communs, en espagnol, d'au moins trois espèces similaires d'arbres originaires du Gran Chaco, en Amérique latine : Schinopsis lorentzii (quebracho colorado santiagueño), de la famille des Anacardiaceae ; Schinopsis balansae (quebracho colorado chaqueño), de la même famille ;
Aspidosperma quebracho-blanco (quebracho blanc), de la famille des Apocynaceae.
Ces trois espèces sont riches en tanin et fournissent un bois très dur, particulièrement résistant. Leur nom provient de l'espagnol quiebrahacha, qui signifie brise-hache.
Rugosité
Tanins
Vernis en phase aqueuse
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
This study evaluated the effect of accelerated weathering on the adhesion strength and surface roughness of beech wood (Fagus orientalis) treated with mimosa and quebracho extracts and coated with polyurethane, water-based, and cellulosic varnishes. Untreated beech wood blocks and beech wood blocks treated with Tanalith-E were used as control samples. Test samples were exposed to accelerated weathering processes of 100 and 300 h. According to the test results, the mean adhesion strength of the wood samples impregnated with mimosa and quebracho tannins decreased by a maximum of 20%, while increases in the mean surface roughness (Ra) were detected. The highest adhesion strength and lowest mean surface roughness were obtained with polyurethane varnish. Moreover, the mean adhesion strength increased with the accelerated weathering up to 100 h and then decreased thereafter. As a result of the weathering process, the mean surface roughness increased and was thus negatively affected. |
| Note de contenu : |
- MATERIALS AND METHODS : Wood samples and impregnation process - Coating of the wood surfaces - Accelerated weathering tests - Adhesion strength - Surface roughness - Contact angle (CA) measurement - Scanning electron microscopy (SEM) - Statistical analyses
- RESULTS AND DISCUSSION : Retention of wood specimens - Adhesion strength - Surface roughness |
| DOI : |
10.1007/s11998-016-9841-1 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-016-9841-1.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=27800 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 14, N° 1 (01/2017) . - p. 185-193
Aller sur edunet
Accueil
The effects of tannins on adhesion strength and surface roughness of varnished wood after accelerated weathering in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 14, N° 1 (01/2017)