| Titre : |
Characterization of immiscibly blended polyurethane coatings part 1 : selective staining for enhanced micro-Raman spectroscopy |
| Type de document : |
texte imprimé |
| Auteurs : |
Nicholas W. M. Heller, Auteur ; Clive R. Clayton, Auteur ; Spencer L. Giles, Auteur ; James H. Wynne, Auteur ; Mark E. Walker, Auteur ; Mark J. Wytiaz, Auteur |
| Année de publication : |
2017 |
| Article en page(s) : |
p. 163-175 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Agent mattant
Epoxydes
Matériaux -- Coloration
Pigments
Polyacryliques
Polyols
Polyuréthanes
Réticulation (polymérisation)
Revêtements poudre:Peinture poudre
Spectroscopie Raman
Styrène
Thermodurcissables
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Raman spectroscopy (RS) mapping of the selective infiltration of styrene monomer has been developed as a protocol for polymeric phase identification in resin-blended thermoset powder coatings. Blends of incompatible acrylic polyols, with low and high hydroxyl contents, combined with matting agents and pigments, were crosslinked to produce unique low gloss thermosets. The low reflectance originated from a synergistic effect between the polymeric phase separation and the incorporation of the matting agents and pigments. RS conclusively identified the phases within the blended film using polyester-embedded cross-section samples. Further analysis has revealed that monomeric styrene from the polyester-embedding resin produced the spectroscopic handle necessary for domain identification. Preferential infiltration of styrene was therefore investigated through dip and vapor staining of the blended and individual resin films. The spectroscopic handle had manifested through the consistent infiltration of styrene within the low hydroxyl film. The contamination in the cross-sections was eliminated when an epoxy-embedding resin was utilized, which produced no such marker peak in the ensuing spectra. These observations led to the development of the described selective staining protocol for micro-Raman analysis, which enabled very reproducible results for enhanced chemical mapping of phase-separated coatings. |
| Note de contenu : |
- EXPERIMENTAL : Coating preparation - Optical microscopy - Differential scanning calorimetry (DSC) - Raman spectroscopy - Cross-section sample preparation - Styrene vapor staining
- RESULTS AND DISCUSSION : DSC analysis and optical microscopy of the blend surface - Raman spectroscopy of coating surfaces and embedded cross-sections - Domain identification by Raman mapping - Controlled staining with styrene vapor |
| DOI : |
10.1007/s11998-016-9839-8 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-016-9839-8.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=27798 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 14, N° 1 (01/2017) . - p. 163-175
Aller sur edunet
Accueil
Characterization of immiscibly blended polyurethane coatings part 1 : selective staining for enhanced micro-Raman spectroscopy in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 14, N° 1 (01/2017)