Preparation of hydrophobic nanosilica-filled polyacrylate hard coatings on plastic substrates / Chao-Ching Chang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 3 (05/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 3 (05/2014) . - p. 381-386 Titre : Preparation of hydrophobic nanosilica-filled polyacrylate hard coatings on plastic substrates Type de document : texte imprimé Auteurs : Chao-Ching Chang, Auteur ; Tai-Yueh Oyang, Auteur ; Yu-Chen Chen, Auteur ; Feng-His Hwang, Auteur ; Liao-Ping Cheng, Auteur Année de publication : 2014 Article en page(s) : p. 381-386 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Analyse thermique Caractérisation Dureté (matériaux) Gel de silice Hexaacrylate de dipentaérythritol Hydrophobie Nanoparticules -- Synthèse Polyacrylates Polyéthylène téréphtalate Polyméthacrylate de méthyle Le poly(méthacrylate de méthyle) (souvent abrégé en PMMA, de l'anglais Poly(methyl methacrylate)) est un polymère thermoplastique transparent obtenu par polyaddition dont le monomère est le méthacrylate de méthyle (MMA). Ce polymère est plus connu sous son premier nom commercial de Plexiglas (nom déposé), même si le leader global du PMMA est Altuglas International9 du groupe Arkema, sous le nom commercial Altuglas. Il est également vendu sous les noms commerciaux Lucite, Crystalite, Perspex ou Nudec. Réticulation (polymérisation) Revêtements -- Séchage sous rayonnement ultraviolet Sol-gel, Procédé Stabilité thermique Structure chimique Index. décimale : 667.9 Revêtements et enduits Résumé : Colloidal silica nanoparticles synthesized from tetraethoxysilane via a sol–gel process were surface-modified first by 3-(trimethoxysilyl)propyl methacrylate, and then by trimethylethoxysilane (TMES). The former agent acts both as a coupling agent and as a C=C provider, whereas the latter agent is used to prevent particle aggregation and to increase hydrophobicity of the coating. The modified silica particles were UV-cured together with the monomer, 2-hydroxyethyl methacrylate (2-HEMA), and the crosslinking agent, dipentaerythritol hexaacrylate (DPHA), to form highly transparent hard coatings on plastic (PMMA and PET) substrates. Both differential scanning calorimetric and thermal gravimetric analyses of the hybrid materials indicated enhanced thermal stability with respect to the neat HEMA–DPHA copolymer. Furthermore, due to the incorporation of TMES, hydrophobicity of the hybrid coating increased considerably with increasing modified silica content. In the extreme case, an antiabrasive hard coating (7H on PMMA) with a water contact angle of 99° was obtained at the silica content of 15 wt%. Note de contenu : - EXPERIMENTAL : Materials - Preparation of silica nanoparticles - Preparation of hybrid coatings - Characterization - RESULTS AND DISCUSSION : Chemical structure analysis - Thermal analysis - Hardness and physical properties DOI : 10.1007/s11998-013-9540-0 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9540-0.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21457 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16292	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)