Corrosion protection of mild steel by nano-colloidal polyaniline/nanodiamond composite coating in NaCl solution / Habib Ashassi-Sorkhabi in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 3 (05/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 3 (05/2014) . - p. 371-380 Titre : Corrosion protection of mild steel by nano-colloidal polyaniline/nanodiamond composite coating in NaCl solution Type de document : texte imprimé Auteurs : Habib Ashassi-Sorkhabi, Auteur ; Moosa Es'haghi, Auteur Année de publication : 2014 Article en page(s) : p. 371-380 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Anticorrosion Chlorure de sodium Le chlorure de sodium est un composé chimique de formule NaCl. On l'appelle plus communément sel de table ou de cuisine, ou tout simplement sel dans le langage courant. C'est le principal produit dissous dans l'eau de mer ; on l'appelle alors sel marin. On l'obtient : dans des marais salants par évaporation de l'eau de mer, dans des mines, par extraction du sel gemme (halite) ou en le synthétisant lors de réactions à hautes températures entre du dichlore (Cl2) et du sodium métallique (Na). Le chlorure de sodium est utilisé dans l'industrie chimique pour produire du chlore, de la soude caustique et de l’hydrogène. Colloides Conducteurs organiques Diamant Electrochimie organique Nanoparticules Polyaniline Polymères -- Synthèse Index. décimale : 667.9 Revêtements et enduits Résumé : The polyaniline/nanodiamond (PANI/ND) nanocomposite coating was synthesized on mild steel via electrochemical polymerization using cyclic voltammetry technique. The ultrasonic irradiation was used for effectively dispersing ND particles in electropolymerization solution. The prepared nanocomposite films were found to be nano-colloidal, and very adherent with low porosity. X-ray diffraction and FTIR techniques confirmed the intercalation of the nanoparticles in PANI matrix. The corrosion performance of the coatings was investigated in 3.5% NaCl solution by electrochemical impedance spectroscopy (EIS), polarization, and salt spray methods. The obtained results showed that the presence of ND particles significantly enhanced the corrosion protection performance of the PANI films in corrosive medium. EIS and polarization measurements indicated that the coating resistance and corrosion resistance values for the PANI/ND nanocomposite coating were much higher than that of pure PANI-coated electrode. Also, the results obtained revealed that the protection efficiency of PANI/ND-coated mild steel is achieved about 90% after 3 days. The porosity in PANI/ND nanocomposite coating is almost 18 times lower than that of the PANI coating. Note de contenu : - Electrochemical synthesis of polyaniline on mild steel - X-ray diffraction analysis - FTIR studies - Surface morphology studies - Evaluating the corrosion resistance - Tafel polarization studies - Electrochemical impedance measurements - Salt spray tests - Stability of the PANI/ND coating on mild steel DOI : 10.1007/s11998-013-9546-7 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9546-7.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21456 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16292	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)