| Titre : |
UV protection against photoageing of garment leathers by ZnO nanoparticles : application of nano ZnO in finishing process as photocatalyst |
| Type de document : |
texte imprimé |
| Auteurs : |
Bekir Yilmaz, Auteur ; Ersin Onem, Auteur ; Ali Yorgancioglu, Auteur ; Eser Eke Bayramoglu, Auteur |
| Année de publication : |
2016 |
| Article en page(s) : |
p. 321-326 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Analyse de variance En statistique, l'analyse de la variance (terme souvent abrégé par le terme anglais ANOVA : ANalysis Of VAriance) est un ensemble de modèles statistiques utilisés pour vérifier si les moyennes des groupes proviennent d'une même population. Les groupes correspondent aux modalités d'une variable qualitative (p. ex. variable : traitement; modalités : programme d'entrainement sportif, suppléments alimentaires ; placebo) et les moyennes sont calculés à partir d'une variable continue (p. ex. gain musculaire).
Ce test s'applique lorsque l'on mesure une ou plusieurs variables explicatives catégorielles (appelées alors facteurs de variabilité, leurs différentes modalités étant parfois appelées "niveaux") qui ont de l'influence sur la loi d'une variable continue à expliquer. On parle d'analyse à un facteur lorsque l'analyse porte sur un modèle décrit par un seul facteur de variabilité, d'analyse à deux facteurs ou d'analyse multifactorielle sinon. (Wikipedia)
Cuir -- Teneur en chrome hexavalent
Cuirs et peaux -- Analyse
Cuirs et peaux -- Finition
Duncan, Test de
Essais accélérés (technologie)
Nanoparticules
Oxyde de zinc
Photocatalyse
Spectrophotométrie
Statistique
|
| Index. décimale : |
675 Technologie du cuir et de la fourrure |
| Résumé : |
In this study, zinc oxide nano-particles, known to have photocatalytic and high UV protection properties, were used in the finishing process to prevent chromium(VI) formation as a result of photoageing in the garment leather products. The researches were carried out on the chrome-tanned garment leather. Nano zinc oxide at the proportions of 0.25%, 0.5% and 1% on nitrocellulose (N/C) emulsion amount were used in the finishing process of leathers. The finished garment leathers were exposed to an artificially accelerated ageing process at 80°C for 24 hours and 80°C/UV for 24 hours. Cr(VI) amounts in each leather sample were evaluated in compliance with ISO/FDIS 17075 standard test method based on the reaction of chromium(VI) with diphenylcarbazide and subsequent colorimetric determination at 540nm by using a double beam Shimadzu 1601 UV visible region spectrophotometer. The leathers finished using nano ZnO were compared to control samples and the way in which ZnO nanoparticles affect Cr(VI) formation was statistically examined by the analysis of variance (ANOVA) and Duncan test. According to research results, it was determined that Cr(Vl) amounts arising in the garment leathers after photoageing were rather high and that the use of nano zinc oxide in finishing process substantially eliminated Cr(VI) formation statistically by providing high UV protection. 18,31 ± 2.46ppm of Cr(Vl) occured under 80°C/UV for 24 hours was decreased to less than 3ppm by 1% of nano ZnO. Using 0.25% and 0.5% of nano ZnO on the amount of N/C emulsion applied also reduced the levels of Cr(VI) to under 3ppm. |
| Note de contenu : |
- Materials
- Finishing process
- Accelerated ageing treatment
- Chromium(VI) analysis in leather samples
- Statistical analysis |
| En ligne : |
https://drive.google.com/file/d/1qbW5iXWrsAc8w1-UC2R8g8eRvnV1dGRe/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=27668 |
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 100, N° 6 (11-12/2016) . - p. 321-326