Cure kinetics of several epoxy-amine systems at ambient and high temperatures / Monoj Pramanik in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 2 (03/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 2 (03/2014) . - p. 143-157 Titre : Cure kinetics of several epoxy-amine systems at ambient and high temperatures Type de document : texte imprimé Auteurs : Monoj Pramanik, Auteur ; Eric W. Fowler, Auteur ; James W. Rawlins, Auteur Année de publication : 2014 Article en page(s) : p. 143-157 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Amines Une amine est un composé organique dérivé de l'ammoniac dont certains hydrogènes ont été remplacés par un groupement carboné. Si l'un des carbones liés à l'atome d'azote fait partie d'un groupement carbonyle, la molécule appartient à la famille des amides. Découvertes en 1849, par Wurtz les amines furent initialement appelées alcaloïdes artificiels. On parle d'amine primaire, secondaire ou tertiaire selon que l'on a un, deux ou trois hydrogènes substitués. Par exemple, la triméthylamine est une amine tertiaire, de formule N(CH3)3. Typiquement, les amines sont obtenues par alkylation d'amines de rang inférieur. En alkylant l'ammoniac, on obtient des amines primaires, qui peuvent être alkylées en amines secondaires puis amines tertiaires. L'alkylation de ces dernières permet d'obtenir des sels d'ammonium quaternaire. D'autre méthodes existent : 1. Les amines primaires peuvent être obtenues par réduction d'un groupement azoture, 2. Les amines peuvent aussi être obtenues par la réduction d'un amide, à l'aide d'un hydrure, 3. L'amination réductrice permet l'obtention d'amines substituées à partir de composés carbonylés (aldéhydes ou cétones), 4. Les amines primaires peuvent être obtenues par la réaction de Gabriel. Caoutchouc Core-Shell Epoxydes Hautes températures Particules (matières) Réticulants Revêtements -- Séchage sous rayonnement infrarouge proche:Peinture -- Séchage sous infrarouge proche Index. décimale : 667.9 Revêtements et enduits Résumé : Epoxy-crosslinker curing reactions and the extent of the reactions are critical parameters that influence the performance of each epoxy system. The curing of an epoxy prepolymer with an amine functional group may be accompanied by side reactions such as etherification. Commercial epoxy prepolymers were cured with different commercial amines at ambient as well as at elevated temperatures. Singularly, only epoxy–amine reactions were observed with diglycidyl ether of bisphenol-A (DGEBA)-based epoxides in our research even upon post-curing at 200°C. Etherification side reaction was found to occur at a cure temperature of 200°C in epoxides possessing a tertiary amine moiety. A combined goal of our research was to understand the effect of tougheners on the cure of epoxy–amine blend. To discern the effect of tougheners on the cure, core–shell rubber (CSR) particles were incorporated into the epoxy–amine blend. It was observed that CSR particles did not restrict the system from proceeding to complete reaction of epoxy moieties. Besides, CSR particles were found to accelerate the epoxy-amine reaction at a lower level of epoxy conversion. The lower activation energy of epoxy–amine reaction of CSR incorporated system compared to control supported the catalytic effect of CSR particles on the epoxy-amine reaction of epoxy prepolymer and amine blends. Note de contenu : - EXPERIMENTAL : Materials - Characterization - Near IR (NIR) spectroscopy - Background of application of NIR spectroscopy - Transmission Electron Microscopy (TEM) - RESULTS AND DISCUSSION : Determination of epoxy, primary amine, secondary amine, and total amine hydrogen concentration - Concentration and conversion of epoxy, primary amine, secondary amine, and total amine hydrogen DOI : 10.1007/s11998-013-9565-4 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9565-4.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21160 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16196	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)