[article]
| Titre : |
Study of the properties of novel hybrid coatings under the influence of phase compatibility |
| Type de document : |
texte imprimé |
| Auteurs : |
Huang Dong, Auteur ; Jun Wang, Auteur ; Jijun Tang, Auteur ; Wenjun Shen, Auteur ; Weili Li, Auteur ; Jing Zhang, Auteur ; Zexiao Xu, Auteur |
| Année de publication : |
2016 |
| Article en page(s) : |
p. 691-701 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Copolymérisation
Polyacryliques
Polyaddition
PolydiméthylsiloxaneLe polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones.
Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone.
Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK).
La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones.
Réaction de couplage
Réticulants
Réticulation (polymérisation)
Revêtements organiques
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
In this article, a series of hybrid coatings were prepared and characterized. At first, polydimethylsiloxane modified with siliane coupling agent was copolymerized with acrylate monomers by free radical polymerization to get the hybrid resins. Due to the combination of covalent bond, the prepared hybrid resins were uniform and transparent. Then a series of hybrid resins were cured with tetraethoxysilane and dibutyltin dilaurate as the crosslinker and catalyst, respectively. The blends were loaded onto the substrate, such as tin plate, steel panels, or flat glass, and cured by heating to form hybrid coatings. To study the factors on the properties of the prepared hybrid resins and cured coatings, various measurements were carried out, such as FTIR, TGA, DSC, laser optical microscope, water contact angles, pencil scratch hardness, and the electrochemistry test. Thanks to the combination of covalent bond, the two components dispersed uniformly in the prepared hybrid resins and no cracks were observed from the cured hybrid coatings with an optical microscope. With excellent mechanical properties, thermal stability, corrosion resistance, and hydrophobic property, the prepared hybrid coatings can find application in the heavy-duty chemical industry. |
| Note de contenu : |
- EXPERIMENTAL : Preparation of the hybrid resins - Coating procedure - Characterization
- RESULTS AND DISCUSSION : FTIR measurements - Surface morphology - Thermal properties - Physical properties of the cured hybrid coatings - Anticorrosion behavior |
| DOI : |
10.1007/s11998-015-9776-y |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-015-9776-y.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=26749 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 13, N° 4 (07/2016) . - p. 691-701
[article]
|
Aller sur edunet
Accueil
Study of the properties of novel hybrid coatings under the influence of phase compatibility in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 13, N° 4 (07/2016)