Polyurethane/polyacrylate/silica nanocomposite prepared by seeded emulsion polymerization and the properties of finished leather / Yan Bao in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC), Vol. 97, N° 6 (11-12/2013)  

[article]  inJOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 97, N° 6 (11-12/2013) . - p. 238-243 Titre : Polyurethane/polyacrylate/silica nanocomposite prepared by seeded emulsion polymerization and the properties of finished leather Type de document : texte imprimé Auteurs : Yan Bao, Auteur ; Jianzhong Ma, Auteur ; Junli Liu, Auteur ; Juan Lu, Auteur Année de publication : 2013 Article en page(s) : p. 238-243 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Allongement (mécanique) Dioxyde de silicium Matériaux hybrides Matériaux hybrides -- Propriétés mécaniques Persulfate de potassium Polyacrylates Polymérisation en émulsion Polyuréthanes Résistance à l'humidité Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Sol-gel, Procédé Tétraéthoxysilane Traction (mécanique) Vinyltriéthoxysilane Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : A polyurethane/polyacrylate/silica nanocomposite was prepared by seeded emulsion polymerization using polyurethane as a seed emulsion and potassium persulphate (KPS) as a free radical initiator, in which silica was synthesized via the sol-gel method of tetraethoxysilane (TEOS) and was modified by vinyl triethoxy silane (A-151). The influence of synthesis conditions such as the polyurethane and Si02 content on the physical-mechanical properties and water resistance of polyurethane/polyacrylate/silica nanocomposite was investigated in detail. The tensile strength and elongation at break of nanocomposite films, at first, increases and then decreases with the increasing content of polyurethane. The incorporation of silica leads to improved tensile strength, but the elongation at break decreased. Water uptake measurements confirmed that the water resistance of polyurethane/polyacrylate/silica nanocomposite was improved by the introduction of polyurethane and silica. The improved properties of the leather finished by polyurethane/polyacrylate/silica nanocomposite are shown, in contrast to polyacrylate finish. The water vapour permeability was increased by 7.14% and the water resistance by 30.34%. Note de contenu : - EXPERIMENTAL PROCEDURES : Materials - Preparation of polyurethane/polyacrylate/silicate nanocomposite - Determination of physical mechanical property of composite films - The application as a leather finish - RESULTS AND DISCUSSION : The mechanism of polyurethane/polyacrylate/silica nanocomposite - Effect of polyurethane contents - Effect of SiO2 contents - Applied properties En ligne : https://drive.google.com/file/d/1-2yOt8zi_BXQBufQXKvre1Plc38axXs8/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=20145 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
15837	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)