Effect of surface wettability on transparency in different water conditions / Zhoukun He in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 10, N° 5 (09/2013)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 10, N° 5 (09/2013) . - p. 641-647 Titre : Effect of surface wettability on transparency in different water conditions Type de document : texte imprimé Auteurs : Zhoukun He, Auteur ; Xiaorong Lan, Auteur ; Feng Chen, Auteur ; Ke Wang, Auteur ; Hua Deng, Auteur ; Qin Zhang, Auteur ; Qiang Fu, Auteur Année de publication : 2013 Article en page(s) : p. 641-647 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Dioxyde de silicium Hydrophilie Hydrophobie Mouillabilité Polydiméthylsiloxane Le polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones. Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone. Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK). La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Revêtements:Peinture Surfaces -- Analyse Transparence (optique) Index. décimale : 667.9 Revêtements et enduits Résumé : Water droplets or films which are formed according to surface wettability show different effects on surface transparency. The effects of surface wettability on transparency in different water conditions are worth investigating because the surface usually suffers from the variable environmental water conditions. Herein, superhydrophobic and superhydrophilic surfaces, with negligible differences of physical structure but great differences of chemical composition, are used to investigate for the first time the relationship between surface wettability and transparency in four water conditions, including ambient condition, liquid water, boiling water steam, and ambient conditions after freezing at −4°C for 1 week. The transparency of the superhydrophobic surface is only about 5% lower in 550 nm light wavelength than that of the superhydrophilic surface in ambient conditions, but it is about 24% lower than that of the superhydrophilic surface in liquid water. When the surfaces are exposed to boiling water steam and ambient conditions after freezing at −4°C for 1 week, the superhydrophobic surface also shows lower transparency than the superhydrophilic surface because of increased fogging. However, the transparency shows little difference when the fog evaporates completely. The relationship revealed between surface wettability and transparency in different water conditions will be beneficial in choosing suitable wettability surfaces to satisfy the needed transparency in actual applications. Note de contenu : - EXPERIMENTAL SECTION : Matreials - Sample preparation - Characterization - RESULTS AND DISCUSSION : Surface wettability, morphology, and chemical composition of the coatings - Transparency in ambient conditions and in liquid water - Transparency in boiling water steam and in ambient conditions after freezing at -4°C for 1 week DOI : 10.1007/s11998-013-9490-6 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9490-6.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=19798 [article]

Réservation

Réserver ce document

Exemplaires (2)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
15618	-	Périodique	Bibliothèque principale	Documentaires	Disponible
15679	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)