Utilizing Taguchi design of experiment to study the surface treatment of a nanosilica with an acrylic silane coupling agent and revealing the dispersibility of particles in a urethane acrylate resin / Y. Zamani Ketek Lahijani in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 10, N° 4 (07/2013)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 10, N° 4 (07/2013) . - p. 537-547 Titre : Utilizing Taguchi design of experiment to study the surface treatment of a nanosilica with an acrylic silane coupling agent and revealing the dispersibility of particles in a urethane acrylate resin Type de document : texte imprimé Auteurs : Y. Zamani Ketek Lahijani, Auteur ; Mohsen Mohseni, Auteur ; S. Bastani, Auteur Année de publication : 2013 Article en page(s) : p. 537-547 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Copolymère uréthane acrylate Dispersions et suspensions Fourier, Spectroscopie infrarouge à transformée de Hydrolyse Nanoparticules pH Réaction de couplage Silanes Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Taguchi, Méthodes de (Contrôle de qualité) Taille des particules Thermogravimétrie Traîtements de surface Index. décimale : 667.9 Revêtements et enduits Résumé : This work aims at investigating the dispersibility of a modified hydrophilic nanosilica using methacryloxy propyltrimethoxysilane (MPTMS) in an organic phase, which contains UV-curable urethane acrylate oligomers and monomers with different functionalities. Through a Taguchi design of experiment, the impacts of influencing parameters such as silane coupling agent to silica ratio, hydrolysis ratio as well as treating bath pH were investigated. The optimum condition in which the maximum percentage of modification occurred was observed at higher stoichiometric levels of silane:silica ratio and alkaline pH conditions. Furthermore, statistical analysis demonstrated that hydrolysis ratio was not very significant. Low amounts of turbidity of prepared hybrid coatings indicated that modified particles with higher grafting contents had better dispersion stability in the acrylate resin. Note de contenu : - Experimental - Particle characterization - Preparation of particle-loaded films - Results and discussion - Effect of treatment pH - Effects of silane concentration and hydrolysis - Particle size - Structural studies using FTIR analysis - TGA particles - Elemental analysis of the particles - Performance of particles in urethane acrylate matrix DOI : 10.1007/s11998-013-9471-9 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9471-9.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=19103 [article]

Réservation

Réserver ce document

Exemplaires (2)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
15460	-	Périodique	Bibliothèque principale	Documentaires	Disponible
15594	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)