Formulation and study of corrosion prevention behavior of epoxy cerium nitrate-montmorillonite nanocomposite coated carbon steel / E. Darmiani in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 10, N° 4 (07/2013)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 10, N° 4 (07/2013) . - p. 493-502 Titre : Formulation and study of corrosion prevention behavior of epoxy cerium nitrate-montmorillonite nanocomposite coated carbon steel Type de document : texte imprimé Auteurs : E. Darmiani, Auteur ; I. Danaee, Auteur ; G. R. Rashed, Auteur ; Davood Zaarei, Auteur Année de publication : 2013 Article en page(s) : p. 493-502 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Anticorrosion Epoxydes Matériaux hybrides Métaux -- Revêtements protecteurs Montmorillonite Nanoparticules Nitrate de cérium Spectroscopie d'impédance électrochimique Index. décimale : 667.9 Revêtements et enduits Résumé : Nanocomposite coatings which were applied on carbon steel panels based on epoxy cerium nitrate–montmorillonite (MMT) were synthesized and formulated. Nanoparticles were incorporated into epoxy resin by mechanical and sonication processes. The state of dispersion, dissolution, and incorporation were characterized by optical microscopy, sedimentation tests, X-ray diffraction, and transmission electron microscopy. To investigate anticorrosive properties of nanocomposite coatings, electrochemical impedance spectroscopy and salt spray tests were employed. The experimental results showed that epoxy cerium nitrate–MMT nanocomposite coatings were superior to the neat epoxy in corrosion protection effects. In addition, it was observed that the corrosion protection of nanocomposite coatings was improved as the clay loading was increased up to 4–2 wt% cerium nitrate. Note de contenu : - EXPERIMENTAL : Materials - Preparation of nanocomposites - Sample preparation - Laboratory - RESULTS AND DISCUSSION : Optical microscopy results - Stability - XRD and TEM analysis - Electrochemical impedance spectroscopy - Salt spray test DOI : 10.1007/s11998-012-9463-1 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-012-9463-1.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=19099 [article]

Réservation

Réserver ce document

Exemplaires (2)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
15460	-	Périodique	Bibliothèque principale	Documentaires	Disponible
15594	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)