Crystallization behavior and mechanical properties of nanosilica-reinforced isotactic polypropylene composites |
| Type de document : |
texte imprimé |
| Auteurs : |
J. Li, Auteur ; L.-J. Long, Auteur ; W.-T. He, Auteur ; K. Zhang, Auteur ; Y.-S. Xiang, Auteur ; J. Zhang, Auteur ; M.-M. Zhang, Auteur ; C.-P. Yang, Auteur ; J. Yu, Auteur |
| Année de publication : |
2015 |
| Article en page(s) : |
p. 542-547 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Caractérisation
Charges (matériaux)
Flexion (mécanique)
Gel de silice
Nanoparticules
Polymères -- Propriétés mécaniques
Polymères isotactiques
Polypropylène
Résistance au chocs
SiliceLa silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux.
La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...).
Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale.
Structure cristalline (solide)
Traction (mécanique)
|
| Index. décimale : |
668.9 Polymères |
| Résumé : |
Two different types of inorganic silica fillers, nano-silica powder (NSP) and colloidal silica sol (CSS) were added into isotactic polypropylene (iPP) with low silica content (0.2 wt%) and the influence of the two silica fillers on the crystallization behavior and mechanical properties of iPP were investigated. Differential scanning calorimeter (DSC) results showed that the crystallization temperature of iPP with CSS and NSP were increased by 4.1 °C, and 2.4 °C, respectively. The tensile strength, flexural strength, and izod impact strength of iPP/CSS (33.75 MPa, 33.04 MPa, and 4.80 kJ/m2) were higher than that of iPP/NSP (32.09 MPa, 32.27 MPa, and 4.25 kJ/m2). In addition, the haze value of iPP/CSS was decreased from 37.6 % to 27.6 %, which was 4.7 % lower than that of iPP/NSP (32.3 %). The better performance of CSS as ascribed to its better dispersion ability in iPP matrix than NSP, and it was verified by scanning electron micrograph (SEM) and transmission electron microscope (TEM). Overall, these results indicated that inorganic silica sols had a potential application in the nanoparticle-reinforced composites field. |
| Note de contenu : |
- EXPERIMENTAL : Raw materials - Preparation of iPP/silica composites - Characterization
- RESULT AND DISCUSSION : Crystalline structure and crystallization behavior |
| DOI : |
10.3139/217.3065 |
| En ligne : |
https://drive.google.com/file/d/1TckKt9TRURlEoVI-WZbYRc0LDIc3Gqeg/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=24815 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XXX, N° 5 (11/2015) . - p. 542-547
[article]
|
Aller sur edunet
Accueil
Crystallization behavior and mechanical properties of nanosilica-reinforced isotactic polypropylene composites in INTERNATIONAL POLYMER PROCESSING, Vol. XXX, N° 5 (11/2015)