Nanocrystalline Ni-Co alloy coatings : electrodeposition using horizontal electrodes and corrosion resistance / Babak Bakhit in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 10, N° 2 (03/2013)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 10, N° 2 (03/2013) . - p. 285-295 Titre : Nanocrystalline Ni-Co alloy coatings : electrodeposition using horizontal electrodes and corrosion resistance Type de document : texte imprimé Auteurs : Babak Bakhit, Auteur ; Alireza Akbari, Auteur Année de publication : 2013 Article en page(s) : p. 285-295 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Alliages Anticorrosion Cobalt Dépôt électrolytique Electrodes Matériaux nanocristallins Nickel Le nickel est un élément chimique, de symbole Ni et de numéro atomique 28. Le nickel est un métal blanc argenté qui possède un éclat poli. Il fait partie du groupe du fer. C'est un métal ductile (malléable). On le trouve sous forme combinée au soufre dans la millérite, à l'arsenic dans la nickéline. Grâce à sa résistance à l'oxydation et à la corrosion, il est utilisé dans les pièces de monnaie, pour le plaquage du fer, du cuivre, du laiton, dans certaines combinaisons chimiques et dans certains alliages. Il est ferromagnétique, et est fréquemment accompagné de cobalt. Il est particulièrement apprécié pour les alliages qu'il forme. Revêtement métallique Revêtements protecteurs Index. décimale : 667.9 Revêtements et enduits Résumé : Nanocrystalline Ni–Co alloy coatings containing 0–45 wt% Co were electrodeposited using horizontal electrodes in a modified Watts bath. Different techniques including scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction, microindentation, and potentiodynamic polarization were used to characterize the alloy coatings. Properties of the alloy coatings were investigated as a function of the cobalt ion concentration (Co2+) in the bath. It was observed that the alloy codeposition exhibits anomalous behavior. Co content in the alloy coatings increases with increasing Co2+ in the bath and with electrolyte agitation. Morphology and grain size of alloy coatings are greatly affected by Co content. By increasing Co content, surface morphology of the alloy coatings changes from pyramidal to spherical. Microhardness of the alloy coatings increases with increasing Co content mainly due to decreasing grain size that follows the Hall–Petch relation. In addition, Ni–17 wt% Co alloy exhibits better corrosion resistance compared to pure Ni and other Ni–Co alloy coatings. The higher corrosion resistance of Ni–17 wt% Co coating is discussed based on its phase structure, grain size, and preferred orientation. Note de contenu : - EXPERIMENTAL METHODS AND MATERIALS - RESULTS AND DISCUSSION : Effects of bath concentration and electrolyte agitation - Morphology and phase structure - Microhardness - Corrosion resistance - Comparing overall properties DOI : 10.1007/s11998-012-9437-3 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-012-9437-3.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=18253 [article]

Réservation

Réserver ce document

Exemplaires (3)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
14920	-	Périodique	Bibliothèque principale	Documentaires	Disponible
15125	-	Périodique	Bibliothèque principale	Documentaires	Disponible
15592	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)