| Titre : |
Study of mechanical behavior, deformation, and fracture of nano-multilayer coatings during microindentation and scratch test |
| Type de document : |
texte imprimé |
| Auteurs : |
Kaouthar Khlifi, Auteur ; Hafedh Dhiflaoui, Auteur ; Lassaad Zoghlami, Auteur ; Ahmed Ben Cheikh Larbi, Auteur |
| Année de publication : |
2015 |
| Article en page(s) : |
p. 513-524 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique.
L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1.
C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple.
Couches minces multicouches
Dépôt en phase vapeur
Dureté VickersLa mesure de dureté Vickers se fait avec une pointe pyramidale normalisée en diamant de base carrée et d'angle au sommet entre faces égal à 136°. L'empreinte a donc la forme d'un carré ; on mesure les deux diagonales d1 et d2 de ce carré à l'aide d'un appareil optique. On obtient la valeur d en effectuant la moyenne de d1 et d2. C'est d qui sera utilisé pour le calcul de la dureté. La force et la durée de l'appui sont également normalisées.
Endommagement (mécanique)
Essais dynamiques
Indentation des matériaux
Métaux -- Revêtements protecteurs
Microstructures -- Analyse
Nanotechnologie
Nitrure de titane
Rayures
Revêtements multicouches
Rupture (mécanique)
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Nano-multilayer PVD thin films were deposited on 100C6 (AISI 52100) steel substrate by a PVD magnetron sputtering system. The morphological and microstructural properties were evaluated by using atomic force microscopy and scanning electron microscopy. Residual stresses in all coatings were determined by XRD using the sin2ψ method. Microindentation and scratch tests were performed, respectively, with a Vickers hardness testing machine and scratch test. These tests were carried out on several coatings with various structures, and compositions TiN single layer, TiAlN multilayer, and TiN/TiAlN nano-multilayer. Hardness measurements were performed by using Vickers imprint using the Jonsson and Hogmark model. Critical loads were measured by scratch test. The results show that the coatings topography was dominated by domes and craters which were uniformly distributed over the surface, and all coatings showed a columnar structure. Damage mechanisms under microindentation and scratch depended on coatings structure and composition. Mechanical and structural properties control the damage behavior and the adhesion quality of coatings. The multilayer structure provides an increase in residual stress, hardness, and failure resistance and a decrease in cracks propagation and adhesion resistance. |
| Note de contenu : |
- EXPERIMENTAL DETAILS : Substrate material and coatings deposition - Characterization tests
- RESULTS AND DISCUSSION : Morphological and structural properties - Residual stresses - Microhardness measurements - Micromechanisms of coating damage - Analysis of damage mechanism by scratch test - Adhesion measurement |
| DOI : |
10.1007/s11998-015-9662-7 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-015-9662-7.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=24175 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 12, N° 3 (05/2015) . - p. 513-524