Preparation of metallic coatings with reversibly switchable wettability based on plasma spraying technology / Zhengfeng Li in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 9, N° 5 (09/2012)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 9, N° 5 (09/2012) . - p. 579-587 Titre : Preparation of metallic coatings with reversibly switchable wettability based on plasma spraying technology Type de document : texte imprimé Auteurs : Zhengfeng Li, Auteur ; Yanjun Zheng, Auteur ; Lishan Cui, Auteur Année de publication : 2012 Article en page(s) : p. 579-587 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acétone L'acétone en chimie, (nom officiel IUPAC propanone, aussi connue sous les noms de diméthylcétone, 2-propanone, propan-2-one et béta-cétopropane), de formule chimique CH3COCH3 est le composé le plus simple de la famille des cétones. C'est un isomère du propanal.L’acétone est un liquide transparent, inflammable, d'odeur caractéristique (plutôt fruitée). Sa température de fusion est de -95,4 °C et celle d'ébullition de 56,53 °C. Elle a une densité relative de 0,819 (à 0 °C). C'est un composé très soluble dans l'eau (c'est une molécule polaire à chaîne carbonée courte), dans l'éthanol et dans l'éther. L'acétone est le dérivé le plus simple de la série des cétones aliphatiques et la présence de la double liaison carbone-oxygène lui confère l'essentiel de sa réactivité. Hydrophobie Laurique, Acide Mouillabilité Revêtement métallique Technique des plasmas Index. décimale : 667.9 Revêtements et enduits Résumé : Plasma spray technology was used for the preparation of metallic coatings with reversibly switchable wettability. By spraying Fe, Cr, and Ni mixture powders with different sizes, a micro/submicro-dual scale morphology was obtained. The resultant metallic coating had a superhydrophilic nature, but could be switched into superhydrophobic by spraying an acetone solution of dodecanoic acid while the sprayed surface remained within a temperature range of 100–200°C, although dodecanoic acid itself has a hydrophilic nature. The obtained superhydrophobic coating remained stable if the temperature was below 200°C. The surface wettability could further be switched between superhydrophilicity and superhydrophobicity within a time-scale of only seconds by heating above 220°C and re-spraying the acetone solution of dodecanoic acid in the temperature range of 100–200°C. A chemisorbed molecular layer of dodecanoic acid was responsible for the decrease of the surface energy, and the Fourier transform infrared spectroscopy (FTIR) results suggested that heating the substrate can greatly facilitate the formation of the chemisorbed layer and preferential orientation of the dodecanoic acid molecule. Note de contenu : - EXPERIMENTAL : Materials - Preparation of the superhydrophobic surface - Evaluation of thermal stability and reversible wettability - Characterization - RESULTS AND DISCUSSION : Surface morphology of the prepared coating - Chemical composition immediately after APS - Wettability before and after surface modification - Thermal stability and reversible wettability DOI : 10.1007/s11998-011-9390-6 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-011-9390-6.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=16029 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
14190	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)