[article]
Titre : |
Free-radical reactions and thermal effects in PE during pipe extrusion |
Type de document : |
texte imprimé |
Auteurs : |
Y. Lenger Özcanli, Auteur ; Sh. V. Mamedov, Auteur ; T. Yalçinyuva, Auteur ; V. A. Alekperov, Auteur ; R. Yilgin, Auteur ; A. Durmus, Auteur ; S. Öksüz, Auteur ; B. Aktas, Auteur |
Année de publication : |
2002 |
Article en page(s) : |
p. 333-338 |
Note générale : |
Bibliogr. |
Langues : |
Anglais (eng) |
Index. décimale : |
668.9 Polymères |
Résumé : |
In this study, various effects on the properties of the material, such as free-radical (FR) processes, oxygen induction time (OIT), melting temperature and melting heat are examined during several stages of the polyethylene (PE) pipe extrusion process. The spectra in the Electron Spin Resonance (ESR) are researched between 77 - 293 K and in a wide range of magnetic fields. At 77 K a triplet signal in ESR is observed. The parameters of the signal are ΔHm1 ≅ 1.4 - 1.6 mT; ΔHm² ≅ 1 - 1.2 mT; ΔHm3 ≅ 0.6 - 0.8 mT and g1 ≅ 2.020; g2 ≅ 2.011; g3 ≅ 1.99 and Hyper Fine Structure constant ΔH12 ≅ 2.1 mT; ΔH23 ≅ 5.3 mT. As the temperature increase from 77 K up to 293 K, the signal for g4 ≅ 2.02 (ΔHm4 ≅ 0.7 - 0.8) appears and intensity of signals increase. It is also thought that the triplet observed at 77 K belongs to macroradicals of alkyl (- CH2 - C H - C H2 ), alyl ( ~CH2 C HCH = CHCH2~ ), carboanions and the acyl ( H C O ) radicals of the fourth signal. At room temperature, all the FR's transform into peroxide radicals. The total concentration of the FR's is minimum at 463 K and increases at the outlet of the extruder and the pipe sample.It is observed that the OIT (Oxygen Induction Time) values decrease as one approaches the outlet of the extruder (from 20 - 30 to 10 - 15 minutes), while they increase for the processes of 433 K to 463 K. This event proves that the peroxide radicals form as one passes to room temperature. These results support those of the effects of the extrusion stage on the dynamic-mechanical characteristics [2].
Finally, FR's appear as a result of the breaking of the C - C bonds in the main polymer chains starting from the first step in the extrusion process (433 K) and in the later stages, due to the oxygen in the polymer structure, oxidation processes take place. |
Note de contenu : |
- EXPERIMENTAL METHOD AND PREPARATION OF THE SAMPLES
- EXPERIMENTAL RESULTS : ESR results - The intensity of the signals - Results of DSC - Examination of the DSC melting heats - DSC crystallization phenomena |
DOI : |
10.3139/217.1713 |
En ligne : |
https://drive.google.com/file/d/10Id3n8SM9liRO6-sTtZiJxWqATPvX3Yx/view?usp=drive [...] |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=16022 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XVII, N° 4 (12/2002) . - p. 333-338
[article]
|