Investigating changes in electrochemical properties when nano-silica is incorporated into an acrylic-based polyurethane clearcoat / Hamed Dastmalchian in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 9, N° 2 (03/2012)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 9, N° 2 (03/2012) . - p. 195-201 Titre : Investigating changes in electrochemical properties when nano-silica is incorporated into an acrylic-based polyurethane clearcoat Type de document : texte imprimé Auteurs : Hamed Dastmalchian, Auteur ; Siamak Moradian, Auteur ; Mohammad Mehdi Jalili, Auteur ; Seyed Mojtaba Mirabedini, Auteur Année de publication : 2012 Article en page(s) : p. 195-201 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Nanoparticules Nanotechnologie Polyacryliques Polyols Polyuréthanes Rhéologie Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Spectroscopie d'impédance électrochimique Tension superficielle Vernis -- Additifs Index. décimale : 667.9 Revêtements et enduits Résumé : Two different types of nano-silica (i.e., hydrophilic Aerosil 200 and hydrophobic Aerosil R805) were employed in the preparation of 2-pack acrylic polyol polyurethane nano-coatings so that the electrochemical properties of the resultant coatings could be investigated. Electrochemical impedance spectroscopy was used to evaluate the corrosion performances of such nano-coatings applied onto mild steel substrates that were immersed in 3.5% (w/w) NaCl solutions. It was observed coatings that contained nano-silica increased the barrier properties of the binder, as well as the coatings’ electrochemical resistance compared with pure polyurethane coatings. The surface tension of pure polyurethane was measured by a tensiometer. Rheological properties were also determined at various shear rates by a rotaviscometer. Results showed that the surface tension of hydrophobic nano-silica is very close to the pure polyurethane matrix, giving the better compatibility of the two. This was further confirmed by transmission electron microscopy and by the fact that the hydrophobically filled nano-silica coatings showed shear thinning behavior in the fluid state. Also observed was better corrosion performance of the resultant hydrophobic nano-coatings compared to coatings embedded with hydrophilic nano-silica. Note de contenu : - EXPERIMENTAL METHODS : Raw materials - Preparation of nano-coatings - Tensiometrical properties - Morphological analysis - Rheological studies - Electrochemical behavior - RESULTS AND DISCUSSION : Electrochemical behavior - Morphological observations - Rheological behavior - Electrochemical studies DOI : 10.1007/s11998-009-9222-0 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-009-9222-0.pdf?pdf=button Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=14372 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
14096	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)