Ajouter le résultat dans votre panierA comparative study of various collagen fibre waste as oil sorbent materials / Weining Du in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC), Vol. 99, N° 6 (11-12/2015)
Titre : A comparative study of various collagen fibre waste as oil sorbent materials Type de document : texte imprimé Auteurs : Weining Du, Auteur ; Han Xiaona, Auteur ; Li Zhengjun, Auteur ; Sun Guolong, Auteur ; Li Lixin, Auteur Année de publication : 2015 Article en page(s) : p. 267-272 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Absorbants et adsorbants
Collagène
Cuirs et peaux -- Déchets -- Recyclage
Epoxydes
Huile de colza
Huiles et graisses
Hydrophobie
Nettoyage
Oligomères
PolydiméthylsiloxaneLe polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones.
Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone.
Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK).
La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones.
Poudre de peaux
SiliconesLes silicones, ou polysiloxanes, sont des composés inorganiques formés d'une chaine silicium-oxygène (...-Si-O-Si-O-Si-O-...) sur laquelle des groupes se fixent, sur les atomes de silicium. Certains groupes organiques peuvent être utilisés pour relier entre elles plusieurs de ces chaines (...-Si-O-...). Le type le plus courant est le poly(diméthylsiloxane) linéaire ou PDMS. Le second groupe en importance de matériaux en silicone est celui des résines de silicone, formées par des oligosiloxanes ramifiés ou en forme de cage (wiki).Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : To compare the potentiel utilization of various collagen fibre wastes from the leather industry, such as raw hide waste, oil-tanned and chrome-tanned wastes, as oil sorbents, a hydrophobic polydimethylsiloxane (PDMS) modified collagen fibre was prepared using raw hide waste and an epoxy-terminated silicone oligomer. We fabricated samples 13y a lyophilization technique utilizing the corresponding hide powder fibre (HPF). The oil sorption capacity, sorption saturation time, and retention capacity of prepared sorbents were studied. The results showed that oil sorption capacity of PDMS-modified HPF for silicone oil and vegetable (rape) oil were 6.98 and 5.58g/g, respectively. This sample exhibited the highest oil sorption capacity. The resuits suggest that with appropriate pore size, high porosity and low apparent surface energy, collagen fibre based sorbent would demonstrate favourable oil sorption characteristics and is very promising for ail cleanup application. Note de contenu : - EXPERIMENTAL PROCEDURES : Materials - Preparation of hide powder fibres (HPFs) and PDMS-modified HPF - Preparation of pie-shaped HPF sorbents - Oil sorption capacity - Oil sorption saturation time - Oil retention capacity - Characterizations
- RESULTS AND DISCUSSION : Oil sorption capacity in pure oil medium - Oil sorption saturation time - Oil retention capacityEn ligne : https://drive.google.com/file/d/1gdQCSjGxM_TPnqo-uzetB6n3UyHHkflr/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25097
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 267-272[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Tanning technique of Crocodylus Niloticus bag leather Type de document : texte imprimé Auteurs : Qiang Taotao, Auteur ; Gao Xin, Auteur ; Chen Yuan, Auteur ; Wang Xianjun, Auteur ; Wang Xuechuan, Auteur Année de publication : 2015 Article en page(s) : p. 273-279 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Crocodile du Nil
Cuirs et peaux -- Finition
Cuirs et peaux de reptiles
Maroquinerie
Sacs à main
Tannage au chrome
Température de retrait
Travail de rivière (cuir)Index. décimale : 675.2 Préparation du cuir naturel. Tannage Résumé : Based on the structural features of Crocodylus niloticus raw hides, the operation points and considerations of each process in beamhouse, tanning and finishing operations are discussed in detail. Methods like multi-step degreasing, strong liming, oxidation-reduction bleaching were used to solve the problems in Crocodyfus niloticus tanning, such as high fat content, cuticle cleaning, colour non-uniformity etc. The processing technology which can be applied to practical production of Crocodylus niloticus leather was devised. With the application of this technology, the finished leather was full, soft, and resilient, with high shrinkage temperature, uniform colour, meeting the regulrements for bag leather. Note de contenu : - EXPERIMENTAL PROCEDURES : Materials and apparatus - Observation of Crocodylus niloticus organizational structure - Determination of shrinkage temperature in the tanning process - Tanning procedure of Crocodylus niloticus belly leather
- RESULTS AND DISCUSSION : Structural characteristics of Crocodylus niloticus belly raw hide - Tanning process of Crocodylus niloticus - Structure of chrome-tanned Crocodylus niloticus leather - The changes of Ts in tanning processEn ligne : https://drive.google.com/file/d/1xcosjurZN3QUj1INZ8gWGT8lSFsF652j/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25098
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 273-279[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Characterization of raw wastewater from tanneries Type de document : texte imprimé Auteurs : Mariliz Gutterres, Auteur ; Jaqueline Benvenuti, Auteur ; Juliana T. Fontoura, Auteur ; Santiago Ortiz-Monsalve, Auteur Année de publication : 2015 Article en page(s) : p. 280-287 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caractérisation
Cuirs et peaux -- Industrie -- Aspect de l'environnement
Cuirs et peaux -- Industrie -- Brésil
Eaux usées -- Analyse
Eaux usées -- Stations de traitements
Tannage -- DéchetsIndex. décimale : 675.2 Préparation du cuir naturel. Tannage Résumé : Due to the constantly increasing requirements and supervisory environmental agencies concerning the release of industrial effluents into receiving waters, industries are looking to property treat their effluents and to achieve efficient removal of contaminants. The leather industry is responsible for the production of liquid effluents with high concentrations of pollutants since most of the process steps are carried out in an aqueous medium. Due to the changes in leather technologies in recent years, it is necessary to know and analyze how tannery effluents vary according to the processing steps performed in different tanneries. This may be used to plan and design unit operations in wastewater treatment plants. In order to contribute to this purpose, this study presents the characterization of raw tannery wastewater and provides and discusses an overview of effluent treatment plants and some particularities of them. The raw effluents were characterized by analysis of pH, turbidity, conductivity, chromium oxide, chlorides, total hardness, total Kjeldahl nitrogen (TKN), ammonia nitrogen, sakis (total, suspended : fixed and volatile, dissolved : fixed and volatile), five-day biochemical oxygen demand (BOD), chemical oxygen demand (COD), phosphorus and total organic carbon (TOC). The test results of the parameters for contaminants for each type of tannery are related to previous researches and discussed. Note de contenu : - LEATHER INDUSTRY AND WASTEWATER
- BRAZILIAN LEATHER INDUSTRY AND WASTWATER TREATMENT PLANTS
- MATERIALS AND METHODS : Tanneries and sampling - Wastewater characterizationEn ligne : https://drive.google.com/file/d/1GrNV99KF5Ge787qjsPGJYHsDDfwWVFqQ/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25100
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 280-287[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Dechroming spent tanning liquor using filtration cake from enzymatic hydrolysis of chromium shavings Type de document : texte imprimé Auteurs : P. Kocurek, Auteur ; Karel Kolomaznik, Auteur ; Michaela Barinova, Auteur ; J. Hendrych, Auteur Année de publication : 2015 Article en page(s) : p. 288-292 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Déchromage
Filtration
Hydrolyse enzymatique
Liqueurs de tannageIndex. décimale : 675.2 Préparation du cuir naturel. Tannage Résumé : The work presented deals with the treatment of spent tanning liquor using the chromium cake from alkall enzymatic hydrolysis of leather shavings, the scheme is seen as a part of complete recycling of chromium in the leather industry.
There is a long-term worldwide effort to keep all chromium under control, ideally in a closed loop, since chromium, especially in its hexavalent form, has a negative impact on the environment and human health. The filtration cake obtained by hydrolysis contains a significant amount of chromium and, due to its alkaline character it could be used for the treatment of spent tanning liquor. The work demonstrates that total dechroming of spent tanning liquor is possible. The efficiency of the process depends on the weight ratio between chromium cake and spent tanning liquor and on the retention time. Using a ratio of 0.3 and a retention time of 1 hour, the dechroming level achieved was 81.6%; for a ratio of 1, the dechroming reached up to 98.3%. Using the tonner ratio, the dechroming level increased to 94.1% atter 6 hours. The treatment process has some limitations —the feed composition plays an important role in the process setup to achieve the high dechroming level.Note de contenu : - EXPERIMENTAL PROCEDURES : Materials - Analyses - Alkaline enzymatic hydrolyis - Spent tanning liquor treatment
- RESULTS AND DISCUSSION : Alkaline enzymatic hydrolysis - Spent liquor treatment - Kinetic of precipitationEn ligne : https://drive.google.com/file/d/1orHl-HxISp4Sv4ssT0FR21CgztymF-IT/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25101
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 288-292[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Measurement of hexavalent chromium in chrome-tanned leather : comparative study of acidic condition extraction with alkaline extraction Type de document : texte imprimé Auteurs : Koki Ogata, Auteur ; Yuki Kumazawa, Auteur ; Yoichi Koyama, Auteur ; Keiji Yoshimura, Auteur ; Koji Takahashi, Auteur Année de publication : 2015 Article en page(s) : p. 293-296 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Analyse quantitative (chimie)
Bases (chimie)
Cuir -- Teneur en chrome hexavalent
Extraction (chimie)
Oxydoréduction
pH -- Mesure
StatistiqueIndex. décimale : 675.2 Préparation du cuir naturel. Tannage Résumé : Hexavalent chromium (Cr)E causes dermatitis and cancer, and is often quantified from chrome-tanned leather. Analysis for Cr6+ is generally carried out after extraction into 0.1 M potassium phosphate buffer (P-buffer pH8.0) according to the method of ISO 17075. However, since the pH value of chrome-tanned leather and sweat due to wear are on the acidic side, the abovea method for Cr6+ should be validated using acidic extracts. In the present study, acidic extracts from chrome-tanned leather were analyzed for Cr6+ comparing the results with those using alkaline extracts.
A sample of commercial chrome-tanned leather was used to investigate the influence of pH an the extractability of Cr6+. Chromium was extracted from the leather with P-buffer (pH3.0-11.0), acidic artificiel perspiration (pH5.5) or 0.2% sodium sulfate (pH5.5). The contents of total chromium (Cr) and Cr6+ in each extract were respectively measured by inductive coupled plasma atomic emission spectroscopy and colorimetry with diphenylcarbazide. Less Cr was extracted in the range of pH5.5-8.0, whereas more Cr was extracted in the more acidic and alkaline regions. By contrast, the amount of Cr6+ extracted increased moderately with increasing pH. When the P-buffer extract (pH8.0) was adjusted to pH3.0-11.0, the amount of Cr6+ increased with increasing pH, suggesting occurrence of a reversible conversion between Cr6+ and Cr3+. The extraction with P-buffer (pH8.0) may thus pravide a falsely high value due to this conversion. P-buffer (pH5.5) showed a significantly higher extraction of than tests with artificiel perspiration (pH5.5) and 0.2% sodium sulfate (pH5.5). The residue remaining after each extraction was re-extracted with a fresh aliquot of the appropriate extractant. The amount of Cr6+ in the second extract with P-buffer (pH5.5) exhibited a Iow extractability (about 9% of the amount of the first), whereas artificiel perspiration (pH5.5), 0.2% sodium sulfate (pH5.5), and P-buffer (pH 8.0) showed a high extractability (about 41-67% of the amount of the first). lt is thus concluded that extracting with P-buffer (pH5.5) is most efficient of the tested extractants for analyzing Cr6+ from chrome-tanned leather.Note de contenu : - Materials
- Extraction of chromium for the leather sample
- Measurement of the redox potential of the extract
- Analytical methods
- Statistical analysisEn ligne : https://drive.google.com/file/d/1dCAAo1C3S3vOZgMvheWua20AaoPSaNgW/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25102
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 293-296[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Hygienic properties of leather finished with formulations containing collagen hydrolysate obtained by acid hydrolysis Type de document : texte imprimé Auteurs : Jan Zarlok, Auteur ; Krzysztof Smiechowski, Auteur ; Malgorzata Kowalska, Auteur Année de publication : 2015 Article en page(s) : p. 297-301 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Absorption
Collagène
Cuirs et peaux -- Finition
Désorption
Hydrolysats de protéines
Hydrolyse
Perméabilité
Polyacryliques
Vapeur d'eauIndex. décimale : 675 Technologie du cuir et de la fourrure Résumé : est results of finished leathers are presented in this paper. Varying proportions of acrylic resin and collagen hydrolysate were used as binding agents. The hydrolysate was produced from waste chromium-tanned hide by means of acid hydrolysis. Sorption, desorption and water vapeur permeability were assayed and softness of leathers finished with mixes of varying collagen hydrolysate contents was determined. The testing has demonstrated that collagen hydrolysate in the finishing mixes improved the hygienic properties of finished leathers (increasing absorption, desorption and water vapour permeability). On the other hand leather softness declined a little.
It has been demonstrated that a new leather finishing mix containing protein hydrolysate recovered from chrome shavings can be proposed.Note de contenu : - Production of collagen hydrolysate
- Application of the finishing mix to leathers
- Determination of water vapour absorption
- Determination of desorption of water vapourEn ligne : https://drive.google.com/file/d/1XdFGiPBFLsHlKztW6uxwsPOYoHL1qepZ/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25103
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 297-301[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Comparison of physico-mechanical and physical-chemical properties of leather tanned using different methods Type de document : texte imprimé Auteurs : Malgorzata Kowalska, Auteur ; Malgorzata Przybylek, Auteur ; Anna Zbikowska, Auteur Année de publication : 2015 Article en page(s) : p. 302-306 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Cuirs et peaux -- Propriétés mécaniques
Déchirure (mécanique)
Douceur (toucher)
Essais dynamiques
Humidité -- Absorption:Eau -- Absorption
Perméabilité
Plasticité
Statistique
Tannage au chrome
Traction (mécanique)
Vapeur d'eauIndex. décimale : 675.2 Préparation du cuir naturel. Tannage Résumé : The aim of this work was to analyse physico-mechanical and physico-chemical properties of chrome leather, chrome-free and no-pickle chrome tanned leather. Leather was tested for tensile and tear strength. In addition, dome plasticity of grain, softness, absorption and permeability of water and water vapour were determined.
The properties of no-pickle leathers tanned with chrome and mineral-free tanned were found to exhibit no significant differences from those tanned using traditional methods, even showing a greater tensile strength. Softness was the sole parameter where a poorer performance was observed. it was preliminarily concluded, therefore, that introduction of more environment-friendly technologies requires a more thorough leather processing at the wet finishing stage in order to arrive at a desired leather quality comparable to that of the chrome tanned leather.En ligne : https://drive.google.com/file/d/15FTru7L4ltMe8pa0hf8UEEG3qHOsITuY/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25104
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 302-306[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Titre : Fibre-forming properties of collagen and gelatin derived from bovine limed-split waste Type de document : texte imprimé Auteurs : Wei Xiangyi, Auteur ; Wenhua Zhang, Auteur ; Bi Shi, Auteur Année de publication : 2015 Article en page(s) : p. 307-311 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Collagène
Cuirs et peaux -- Déchets -- Recyclage
Cuirs et peaux de bovins
GélatineLa gélatine est une substance solide translucide, transparente ou légèrement jaune, presque sans goût et sans odeur, obtenue par l'ébullition prolongée de tissus conjonctifs (peaux) ou d'os d'animaux (principalement porc, bœuf, poisson). Elle possède de nombreuses applications dans le domaine culinaire, la médecine, les industries agroalimentaire et pharmaceutique.
En matière d’étiquetage, la gélatine est considérée par la norme européenne3 comme un ingrédient et non pas comme un additif, c'est pourquoi elle n'a pas de numéro E. Hors Union européenne, elle est considérée par certains pays comme un additif gélifiant et on peut la trouver avec la dénomination E441.
La gélatine est un mélange de protéines obtenu par hydrolyse partielle du collagène extrait de la peau comme la peau de porc (cochon), des os, des cartilages, etc. Les liaisons moléculaires entre les fibres de collagène sont alors brisées. Mélangée à de l'eau, la gélatine forme un gel colloïdal semi-solide thermo-réversible (il fond lorsqu'il est chauffé et recouvre son aspect gélatineux lorsqu'il est refroidi). Sous forme déshydratée, par contre, la gélatine n'a pas de point de fusion et devient friable ou brûle quand elle est chauffée à trop haute températureLa rhéologie de la gélatine se caractérise par un comportement viscoélastique, et des contraintes trop élevées ou appliquées trop rapidement peuvent entraîner une rupture fragile (fracturation) ou ductile6. Le caractère plutôt élastique/fragile ou plutôt visqueux/ductile dépend de la concentration en gélatine de la solution aqueuse et de la température, ainsi que de la durée de la mise sous contrainteLes acides aminés constituant la gélatine sont : la glycine (21 %), la proline (12 %), l'hydroxyproline (12 %), l'acide glutamique (10 %), l'alanine (9 %), l'arginine (8 %), l'acide aspartique (6 %), la lysine (4 %), la sérine (4 %), la leucine (3 %), la valine, la phénylalanine et la thréonine (2 %), l'isoleucine et l'hydroxylysine (1 %), la méthionine et l'histidine (< 1 %) et la tyrosine (< 0,5 %). Ces valeurs sont variables (surtout pour les constituants minoritaires) et dépendent de la source de matériaux bruts et de la technique de préparation. La gélatine est constituée à environ 98-99 % (en poids sec) de protéines et contient 18 acides aminés dont huit des neuf acides aminés essentiels à l'Homme. Elle n'a qu'une relative valeur nutritionnelle du fait de l'absence de tryptophane et de son déficit en isoleucine, thréonine et méthionine; elle possède également un taux inhabituellement élevé d'acides aminés non essentiels, la glycine et la proline (qui sont produits par le corps humain). (Wikipedia)
Glutaraldéhyde
pH
Réticulation (polymérisation)Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : Fibre-forming properties of collagen and gelatin derived from bovine limed-split were investigated. It was found that collagen was capable of assembling into fibres in a salt environment. The morphology of collagen fibres was pH dependent. The collagen fibres formed et pH4-6 were in random state while they were further aggregated into ordered fibre bundles with periodic structures in the pH range of 7-8 (around the isoelectric point of collagen). Meanwhile, the directional collagen fibre bundles growing along the lattice orientation of underlying inorganic substrate were prepared in the presence of KCI. In contrast, gelatin was net able to assemble into fibres in the same conditions since its triple helix structure had been broken. The results of this research might well interpret the phenomena that collagen presented better performances in preparations of collagen/gelatin-based biomaterials, and importantly, be instructive for better utilization of tannery skin wastes. Note de contenu : - EXPERIMENTAL METHODS : Preparation of collagen and gelatin - Glutaraldehyde crosslinking of collagen fibre and surface area measurement - pH-controlled fibre-forming of collagen - Substrate-templated and KCI-regulated fibre-forming of collagen
- RESULTS AND DISCUSSION : Fibre-forming property of collagen and gelatin in salt environment - Controllable fibre-forming of collagen - Substrate-templated and KCI-regulated fibre-forming of collagenEn ligne : https://drive.google.com/file/d/16sbIqMCu5w-3vUh8QnAwBMFu6DiwtkJj/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25108
in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 99, N° 6 (11-12/2015) . - p. 307-311[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17683 - Périodique Bibliothèque principale Documentaires Disponible
Exemplaires (1)
| Code-barres | Cote | Support | Localisation | Section | Disponibilité |
|---|---|---|---|---|---|
| 17683 | - | Périodique | Bibliothèque principale | Documentaires | Disponible |