Elastomer nanocomposites based on NR/EPDM/organoclay : morphology and properties |
| Type de document : |
texte imprimé |
| Auteurs : |
A. Alipour, Auteur ; Ghasem Naderi, Auteur ; G. R. Bakhshandeh, Auteur ; H. Vali, Auteur ; S. Shokoohi, Auteur |
| Année de publication : |
2011 |
| Article en page(s) : |
p. 48-55 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Alliages polymères -- propriétés mécaniques
Caoutchouc
Diffractométrie de rayons X
Ethylène-propylène-diène monomère
Matériaux hybrides
Microscopie électronique en transmission
Montmorillonite
Nanoparticules
Rhéologie
Silicates
|
| Index. décimale : |
668.9 Polymères |
| Résumé : |
Natural rubber/Ethylene Propylene Diene Monomer (NR/EPDM) blends of five different compositions (0/100), (25/75), (50/50), (75/25) and (100/0) with 1, 3, 5 and 7 phr organo-modified nanoclay (Cloisite 15A) were prepared by two-roll mill. The effect of organo-modified layered nanosilicates and composition on the cure characteristics, microstructure, mechanical, and rheological properties of the nanocomposites were studied. Results suggested the intercalation of polymer chains into the silicate layers which was evidenced by d-spacing results of X-ray diffraction patterns. TEM micrographs also directly confirmed XRD results. Mechanical properties of the nanocomposites depicted a nearly 40% percents increase respectively in the tensile modulus of 75NR/25EPDM containing 7 wt.% nanoclay. |
| DOI : |
10.3139/217.2381 |
| En ligne : |
https://drive.google.com/file/d/1XwfY-AUYicC6qKRMSjM60AEWtDdMlj8u/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=11037 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XXVI, N° 1 (03/2011) . - p. 48-55
[article]
|
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheElastomer nanocomposites based on NR/EPDM/organoclay : morphology and properties in INTERNATIONAL POLYMER PROCESSING, Vol. XXVI, N° 1 (03/2011)