Effects of added nanoclay for styrene-acrylic resin on intumescent fire retardancy and CO/CO2 emission / Chih-Shen Chuang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 17, N° 1 (01/2020)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 17, N° 1 (01/2020) . - p. 115-125 Titre : Effects of added nanoclay for styrene-acrylic resin on intumescent fire retardancy and CO/CO2 emission Type de document : texte imprimé Auteurs : Chih-Shen Chuang, Auteur ; Horn-Jiunn Sheen, Auteur Année de publication : 2020 Article en page(s) : p. 115-125 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Argile Combustion Contreplaqué Copolymère styrène acrylique Dioxyde de carbone Emission de polluants Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Intumescence (chimie) Monoxyde de carbone Le monoxyde de carbone est le plus simple des oxydes du carbone. La molécule est composée d'un atome de carbone et d'un atome d'oxygène ; sa formule brute s'écrit CO et sa formule semi-développée C≡O ou |C≡O|. Ce corps composé est à l'état gazeux dans les conditions normales de température et de pression. Le monoxyde de carbone est un gaz incolore, inodore, insipide et non irritant, indétectable par les mammifères bien que particulièrement toxique. Le mélange avec l'air est facile puisque les deux gaz ont une densité proche. Chez l'Homme, il est la cause de nombreuses intoxications domestiques, souvent mortelles, qui peuvent être évitées par l'utilisation d'un détecteur de monoxyde de carbone. Son émanation, provenant d'une combustion incomplète de composés carbonés, est accentuée par une mauvaise alimentation en air frais et/ou une mauvaise évacuation des produits de combustion (ventilation). Nanoparticules Polymères en émulsion Revêtements protecteurs Revêtements:Peinture Index. décimale : 667.9 Revêtements et enduits Résumé : Coating plywood with intumescent paint is an effective approach to ensure fire safety in materials. This study investigated the effects of applying an intumescent coating with nanoclay and different amounts of Cloisite 15A (1%, 3%, 5%, and 10%) on 4-mm plywood panels. The nanoclay coating had a lower total heat release and peak heat release rate than other approaches, and it significantly enhanced the fire retardancy of painted plywood. In addition, nanoclay treated with an organic modifier has better flame retardancy than unmodified nanoclay. Another critical parameter in this study was the concentration of organoclay added to the intumescent coating. Cloisite 15A at a concentration of 1% further enhanced the fire retardancy of plywood. A higher organoclay concentration can reduce CO emissions ; however, it also increases CO2 emissions during combustion. The intumescent char layers containing 1% and 3% organoclay had the most extensive phosphocarbonaceous structures according to Fourier-transform IR spectroscopy and 27Al and 31P nuclear magnetic resonance analyses. Regarding the mechanism of fire performance and CO/CO2 emissions, the addition of 1% and 3% Cloisite 15A to intumescent coatings is recommended; it achieved superior performance to Cloisite 15A at a higher concentration (i.e., 10%). Note de contenu : - EXPERIMENTAL : Materials - Sample preparations - Flammability tests - Thermogravimetric analysis - Fourier-transform IR (FTIR) analysis - Spectroscopy analysis of 27Al and 31P solid-state nuclear magnetic resonance - RESULTS AND DISCUSSION : Cone calorimeter test results for clay and organoclay - Thermal property of intumescent coating with different amounts of organoclay - CO and CO2 emission of intumescent coatings with different concentrations of organoclay - FTIR analysis of different coatings - Solid-state 27Al and 31P NMR analyses of different coatings DOI : 10.1007/s11998-019-00246-x En ligne : https://link.springer.com/content/pdf/10.1007/s11998-019-00246-x.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33732 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21517	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)