| Titre : |
Corrosion resistance of steel treated with different silane/paint systems |
| Type de document : |
texte imprimé |
| Auteurs : |
Belén Chico, Auteur ; D. de La Fuente, Auteur ; M. L. Pérez, Auteur ; M. Morcillo, Auteur |
| Année de publication : |
2012 |
| Article en page(s) : |
p. 3-13 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Anticorrosifs
Anticorrosion
Atmosphère marine
Essais accélérés (technologie)
Essais de brouillard salin
Métaux -- Revêtements protecteurs
Revêtements
Silanes
Spectroscopie d'impédance électrochimique
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
This article reports on a comparative study on the corrosion resistance of low-carbon steel substrates pretreated with different silane solutions and painted. The pure silanes used to pretreat the steel panels were 3-aminopropyltriethoxysilane (?-APS), 3-glycidoxypropyltrimethoxysilane (?-GPS), and bis(3-triethoxysilylpropyl)amine. The study also considered other silane solutions with ureido, amino, and epoxy organofunctional groups, and two bis-functional silanes: bis(?-trimethoxysilylpropyl)amine (BAS) and 1,2-bis(triethoxysilyl)ethane (BTSE). A conventional phosphate-type pretreatment was also applied for reference purposes. The pretreated panels were then finished with an alkyd/polyester aminoplast base paint. As a branch test, an acrylic/urethane paint was also applied. Different tests were conducted to evaluate the anticorrosive ability of the different silane/paint systems: outdoor exposure in an atmosphere of moderate aggressivity; accelerated corrosion test (salt fog test); and electrochemical impedance spectroscopy (EIS). The results show that the steel pretreated with certain silanes, especially ?-APS, yields similar results to steel subjected to conventional phosphate pretreatment. |
| Note de contenu : |
- Silane chemistry
- EXPERIMENTAL : Specimen preparation - Aim - Adhesion test - Atmospheric exposure test - Salt spray test - Electrochemical impedance spectroscopy test
- RESULTS AND DISCUSSION : Outdoor test - Exposure test in salt fog cabinet - Electrochemical test - |
| DOI : |
10.1007/s11998-010-9300-3 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-010-9300-3.pdf?pdf=button |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=14350 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 9, N° 1 (01/2012) . - p. 3-13
Aller sur edunet
Accueil
Corrosion resistance of steel treated with different silane/paint systems in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 9, N° 1 (01/2012)