High scrub and low-VOC emulsion / Touria Gharrafi in POLYMERS PAINT COLOUR JOURNAL - PPCJ, Vol. 201, N° 4561 (06/2011)  

[article]  inPOLYMERS PAINT COLOUR JOURNAL - PPCJ > Vol. 201, N° 4561 (06/2011) . - p. 29-31-34 Titre : High scrub and low-VOC emulsion Type de document : texte imprimé Auteurs : Touria Gharrafi, Auteur ; Françoise Decocq, Auteur ; Delphine Uwukunda, Auteur ; Claude Nootens, Auteur Année de publication : 2011 Article en page(s) : p. 29-31-34 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : acrylique, Acide L'acide acrylique ou acide acroléïque ou acide prop-2-énoïque est un composé organique de formule brute C3H4O2 et de formule semi-développée CH2=CHCOOH. C'est un acide carboxylique et un alcène vinylique, et se présente comme un liquide incolore à l'odeur âcre. L'acide acrylique et ses esters, les acrylates, sont utilisés dans la fabrication de matières plastiques, dans les peintures acryliques et dans divers autres polyacryliques qui ont de multiples usages. Copolymères Fenêtres en matières plastiques Frottements (mécanique) Latex pH Résistance à l'abrasion Résistance au lavage Revêtement mural:Peinture murale Revêtements -- Propriétés chimiques:Peinture -- Propriétés chimiques Revêtements -- Propriétés mécaniques:Peinture -- Propriétés mécaniques Revêtements décoratifs:Peinture décorative Revêtements en bâtiment:Peinture en bâtiment Revêtements en phase aqueuse:Peinture en phase aqueuse Sulfonates Surfactants Vinyle sulfonate de sodium Index. décimale : 667.9 Revêtements et enduits Résumé : In order to design a low VOC VeoVa based latex with a high scrub resistance, the latex needs preferably to be a terpolymer stabilised by surfactant with functional sulphonate based monomer and silane based monomer. Note that some low amount of colloid is also possible as long as it does not increase significantly the particle size of the latex. Moreover, the latex should be preferably formulated with unsaturated non-ionic surfactant and therefore it needs to be prepared with a monomer pre-emulsion using a minimum of anionic surfactant. The temperature of polymerisation should be as low as possible. Based on this, a new VA/VeoVa 10/BA (70/20/10) surfactant stabilised latex has been prepared and has demonstrated a higher washability resistance and wet abrasive scrub resistance compared to a conventional surfactant-stabilised terpolymer latex at 80% PVC interior matt paint (figures 10 and 11). Finally, this new VeoVa-based terpolymer has been formulated in an exterior matt paint formulation at 40% PVC. The wet abrasive scrub resistance has been measured and demonstrates the improved scrub resistance of the new terpolymer as seen in figure 12. Alkali resistance of the exterior paint has been determined using an in-house early efflorescence test. As it can been seen in figure 13, the efflorescence resistance of the VeoVa terpolymer is quite close to a commercial all-acrylic and far better than the one observed for the other commercial latices evaluated. In conclusion, the VeoVa 10-based terpolymer has clearly demonstrated a higher scrub resistance than the conventional VeoVa 10 based terpolymer. It can be used in interior and exterior paint formulations on alkali substrates. En ligne : https://drive.google.com/file/d/17FMCiR8yj9XQCaD2TyU7f3_5OVorT5ok/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=11968 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
013131	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)